pa/66 TAROMID A 280 R1

General
Material Status	Commercial: Active
Availability	Europe
Additive	Mold ReleaseUV Stabilizer
Features	Good Chemical ResistanceGood Impact ResistanceGood Mold Release Good UV ResistanceOil ResistantSolvent Resistant
Appearance	Colors Available
Forms	Pellets
Processing Method	Injection Molding

pa/66 TAROMID A 280 R1 及其它型号：

 TAROMID A 280 K6 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 MB3 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 MT6 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 MT8 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 R1 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 R2 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 R3 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 X0 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 Z1 G6 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 Z1 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 Z2 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 Z3 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 Z4 Taro Plast S.p.A. Nylon 66
 TAROMID A 280 Taro Plast S.p.A. Nylon 66
 TAROMID A 280S Taro Plast S.p.A. Nylon 66

 

特性

1、 尼龙容易受潮。在在大气中，PA的平衡吸水率为3.5%、PA66为2.5%、PA610为1.5%，PA1010为0.8%，尼龙含水量对其力学性能有较大的影响。在溶融状态下，水分的存在，会引起尼龙的水解而导致分子量下降，使制品机械性能下降，还会在成型中使制品表面出现气泡、银丝和斑纹等缺陷。所以成型前必须充分干燥。

2、 尼龙熔体粘度低、流动性大，喷嘴会产生“流延”现象。浪费原料，污染喷嘴。如果用螺杆式注射机成型，注射时，熔体会在螺杆和料筒壁之间出现逆流，使注塑不准，所以，尼龙在螺杆式注射机成型时，在螺杆端必须安装止逆环。

3、 尼龙是结晶性高聚物。熔点明显，而且较高，所以，尼龙需要在较高温度下成型，熔融状态的尼龙热稳定性较差，易分解。因此必须严格控制工艺条件。

4、 尼龙的成型性收缩率大，对于制造高精密度的制品，模具设计应在试验的基础上确定其尺寸，成型工艺应严格控制。

pa/66 TAROMID A 280 R1 价格优惠，质量保证。

pa/66 TAROMID A 280 R1 材料产地证明 SGS,MSDS.UL黄卡

pa/66 TAROMID A 280 R1 东莞市艾博（国际）塑胶进口出口有限公司现货供应 pa/66 系列产品可随货提供原材料物性，原材料产地证明SGS.MSDS.UL黄卡等相关详细资料，可开具17%增值税发票.公司秉着“以诚为本，以信为用”的经营理念。与客户是建立在互惠、互利、互信的基础上长期合作。共创双赢局面，愿与各界人士真诚合作，共同发展，携手共创辉煌的明天.

欢迎来人来电咨询洽谈：

直线：0769-88038808

传真：0769-88768175

邓小姐：13728215822

E-mail:abba2010@163.com

网址：www.abplas.com.cn