Sicoflex S302 ABS

ABS 17% glass fibre filled
General
Material Status	Commercial: Active
Availability	Europe
Filler / Reinforcement	Glass Fiber Reinforcement, 17% Filler by Weight

Sicoflex S302 ABS 及其它型号：

 Sicoflex 100A Ravago Group ABS
 Sicoflex 100O Ravago Group ABS
 Sicoflex 2000HG Ravago Group ABS
 Sicoflex 469 Ravago Group ABS
 Sicoflex 91 Ravago Group ABS
 Sicoflex 95 Ravago Group ABS
 Sicoflex 99 Ravago Group ABS
 Sicoflex ABS MZ340 Ravago Group ABS
 Sicoflex ABS MZ341 Ravago Group ABS
 Sicoflex ABS MZ342 Ravago Group ABS
 Sicoflex CRF Ravago Group ABS
 Sicoflex FP454 Ravago Group ABS
 Sicoflex S209 Ravago Group ABS
 Sicoflex S299 Ravago Group ABS
 Sicoflex S302 Ravago Group ABS
 Sicoflex S309 Ravago Group ABS
 Sicoflex S358 Ravago Group ABS
 Sicoflex S433 Ravago Group ABS
 Sicoflex S454 Ravago Group ABS
 Sicoflex S460 Ravago Group ABS
 Sicoflex S471 Ravago Group ABS
 Sicoflex S475 Ravago Group ABS

 

二.ABS塑料加工特性:

ABS同PS一样是一种加工性能优良的热塑性塑料，可用通用的加工方法加工。
ABS的熔体流动性比PVC和PC好，但比PE、PA及PS差，与POM和HIPS类似；ABS的流动特性属非牛顿流体，其熔体粘度对加工温度和剪切速率都有关系，但对剪切速率更为敏感。

ABS的热稳定性好，不易出现降解现象。ABS的吸水性较高，加工前应进行干燥处理。一般制品的干燥条件为温度80~85℃，时间2~4h；对特殊要求的制品（如电镀）的干燥条件为温度70~80℃，时间18~18h。
ABS制品在加工中易产生内应力，内应力的大小可通过浸入冰乙酸中检验；如应力太大和制品对应力开裂绝对禁止，应进行退火处理，具体条件为放于70~80℃的热风循环干燥箱内2~4h，再冷却至室温即可。

三.加工方法：

ABS可用注塑、挤出、压延、吸塑及吹塑等方法成型加工，并以注塑法最广，挤出法次之。

1.注塑 选用柱塞式注塑机的成型温度为180~230℃，而选用螺杆式注塑机的成型温度为160~220℃；对表面光泽度要求高的制品模具温度为60~80℃，而一般制品模具温度为50~60℃即可；对薄壁制品注塑压力为130~150Mpa，而对厚壁制品注塑压力则为60~70Mpa。

2.挤出 可生产管材、板材、片材及型材等，挤出机的L/D为18~22，压缩比为2.5~3。以管材为例，挤出成型的工艺条件为：料筒温度160~180℃，机头温度为175~195℃

3.吸塑成型 吸塑成型的加热温度可控制在140~180℃范围内，并以150℃最佳。

Sicoflex S302 ABS 价格优惠，质量保证。

Sicoflex S302 ABS 原材料产地证明 SGS,MSDS.UL黄卡

Sicoflex S302 ABS 东莞市艾博（国际）塑胶进口出口有限公司现货供应 ABS 全系列产品可随货提供原材料物性，原材料产地证明SGS.MSDS.UL黄卡等相关详细资料，可开具17%增值税发票.公司秉着“以诚为本，以信为用”的经营理念。与客户是建立在互惠、互利、互信的基础上长期合作。共创双赢局面，愿与各界人士真诚合作，共同发展，携手共创辉煌的明天.

欢迎来人来电咨询洽谈：

直线：0769-88038808

传真：0769-88768175

邓小姐：13728215822

E-mail:abba2010@163.com

网址：www.abplas.com.cn