PA66 PLUSTEK RA320G3

Physical Properties	Metric	English	Comments
Density	1.14 g/cc	0.0412 lb/in3	ISO 1183
Moisture Absorption at Equilibrium	2.8 %	2.8 %	50% RH; ISO 62
Water Absorption at Saturation	8.5 %	8.5 %	ISO 62
Linear Mold Shrinkage	0.014 - 0.018 cm/cm	0.014 - 0.018 in/in	ISO 2577
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	115	115
Tensile Strength, Yield	90.0 MPa	13100 psi	ISO 527
Elongation at Break	15 %	15 %	ISO 527
Flexural Strength	120 MPa	17400 psi	ISO 178
Flexural Modulus	2.70 GPa	392 ksi	ISO 178
Izod Impact, Notched (ISO)	4.50 kJ/m2	2.14 ft-lb/in2	ISO 180

PA66 PLUSTEK RA314G50及其它型号： 

PA66 PLUSTEK PA325G5 Polyram 

PA66 PLUSTEK PA325G6 Polyram 

PA66 PLUSTEK PA340S05        Polyram 

PA66 PLUSTEK PA340S4 Polyram 

PA66 PLUSTEK PA340S6 Polyram 

PA66 PLUSTEK PA340S8 Polyram 

PA66 PLUSTEK PA341G9 Polyram 

PA66 PLUSTEK PA350M4 Polyram 

PA66 PLUSTEK PA350M6 Polyram 

PA66 PLUSTEK PA351M8 Polyram 

PA66 PLUSTEK PA352M6 Polyram 

PA66 PLUSTEK PA355M6 Polyram 

PA66 PLUSTEK PA360G6 Polyram 

PA66 PLUSTEK PA4501G6        Polyram 

PA66 PLUSTEK PA4801G6        Polyram 

PA66 PLUSTEK PA4802G6BK10 Polyram 

特性

1、 尼龙容易受潮。在在大气中，PA的平衡吸水率为3.5%、PA66为2.5%、PA610为1.5%，PA1010为0.8%，尼龙含水量对其力学性能有较大的影响。在溶融状态下，水分的存在，会引起尼龙的水解而导致分子量下降，使制品机械性能下降，还会在成型中使制品表面出现气泡、银丝和斑纹等缺陷。所以成型前必须充分干燥。 

2、 尼龙熔体粘度低、流动性大，喷嘴会产生“流延”现象。浪费原料，污染喷嘴。如果用螺杆式注射机成型，注射时，熔体会在螺杆和料筒壁之间出现逆流，使注塑不准，所以，尼龙在螺杆式注射机成型时，在螺杆端必须安装止逆环。 

3、 尼龙是结晶性高聚物。熔点明显，而且较高，所以，尼龙需要在较高温度下成型，熔融状态的尼龙热稳定性较差，易分解。因此必须严格控制工艺条件。 

4、 尼龙的成型性收缩率大，对于制造高精密度的制品，模具设计应在试验的基础上确定其尺寸，成型工艺应严格控制。

PA66 PLUSTEK RA320G3　价格优惠，质量保证。

PA66 PLUSTEK RA320G3　原材料产地证明 SGS,MSDS.UL黄卡

PA66 PLUSTEK RA320G3　东莞市艾博（国际）塑胶进口出口有限公司现货供应 PA66 全系列产品可随货提供原材料物性，原材料产地证明SGS.MSDS.UL黄卡等相关详细资料，可开具17%增值税发票.公司秉着“以诚为本，以信为用”的经营理念。与客户是建立在互惠、互利、互信的基础上长期合作。共创双赢局面，愿与各界人士真诚合作，共同发展，携手共创辉煌的明天.

欢迎来人来电咨询洽谈：

直线：0769-88038808

传真：0769-88768175

邓小姐：13728215822

E-mail:abba2010@163.com

网址：www.abplas.com.cn