Ipethene 113 LDPE

General
Material Status	Commercial: Active
Availability	Africa & Middle EastAsia PacificEurope
Additive	Heat StabilizerMedium AntiblockMedium Slip
Features	BHT FreeHeat StabilizedLow DensityMedium AntiblockingMedium Slip Opticals
Uses	BagsFilmLinersPackagingPouches - Flexible PackagingShrink Wrap
Agency Ratings
Forms	Pellets
Processing Method	ExtrusionFilm Extrusion

Ipethene 113 LDPE 及其它型号：

 Ipethene 100 Carmel Olefins Ltd. LDPE
 Ipethene 111 Carmel Olefins Ltd. LDPE
 Ipethene 113 Carmel Olefins Ltd. LDPE
 Ipethene 210 Carmel Olefins Ltd. LDPE
 Ipethene 213 Carmel Olefins Ltd. LDPE
 Ipethene 320 Carmel Olefins Ltd. LDPE
 Ipethene 322 Carmel Olefins Ltd. LDPE
 Ipethene 323 Carmel Olefins Ltd. LDPE
 Ipethene 4203 Carmel Olefins Ltd. LDPE
 Ipethene 470 Carmel Olefins Ltd. LDPE
 Ipethene 600 Carmel Olefins Ltd. LDPE
 Ipethene 670 Carmel Olefins Ltd. LDPE
 Ipethene 810 Carmel Olefins Ltd. LDPE
 Ipethene 830 Carmel Olefins Ltd. LDPE
 Ipethene 900 Carmel Olefins Ltd. LDPE

 

 

LDPE性能与介绍

LDPE受热后，随温度升高，结晶逐渐减少，结晶部分完全消失，聚乙烯就融化，此时的温度为熔点。聚乙烯的密度升高，结晶度升高，熔点也随升高，所以密度不同聚乙烯，其熔点不同。LLDPE的熔点为120～125℃，于H P-LDPE与HDPE之间。共聚单体的LLDPE，熔点高低随其共聚单体的碳原子的增减而变动，碳原子数增多熔点升高。由LLDPE熔点比H P-LDPE高，模型制品在较高温度下脱模，又快又干净。因LLDPE熔点范围比H P-LDPE，    

LLDPE薄膜，热合强度高。 　　

LDPE在温度升高时的流动性和在增加荷重时的变化，主要受分子量的影响。由于测定聚乙烯的熔体流动速率比测定分子量容易，因而通常以熔体指数(MI)，或熔体流动指数(MFI)来表示聚乙烯的分子量特性。在熔融状态下，LDPE熔体粘度是分子量函数，随分子量增高加大。分子量相同，温度升高熔体粘度降低。常温下LDPE密度有不同韧性。低温LDPE自然有良好韧性，脆析温度较低，与分子量有关。LDPE分子量增高，温度下降，值为-140℃。分子量相同情况下，线型结构的LLDPE与HDPE的熔体粘度要比非线型结构的H P-LDPE大。熔体指数相同情况下，H P-LDPE的熔体粘度明显低于LLDPE和HDPE，前者加工时的熔体流动性明显好后两者，螺杆负荷小，发热量也小。

 

Ipethene 113 LDPE 价格优惠，质量保证。

Ipethene 113 LDPE原材料产地证明 SGS,MSDS.UL黄卡

Ipethene 113 LDPE 东莞市艾博（国际）塑胶进口出口有限公司现货供应 LDPE 全系列产品可随货提供原材料物性，原材料产地证明SGS.MSDS.UL黄卡等相关详细资料，可开具17%增值税发票.公司秉着“以诚为本，以信为用”的经营理念。与客户是建立在互惠、互利、互信的基础上长期合作。共创双赢局面，愿与各界人士真诚合作，共同发展，携手共创辉煌的明天.

欢迎来人来电咨询洽谈：

直线：0769-88038808

传真：0769-88768175

邓小姐：13728215822

E-mail:abba2010@163.com

网址：www.abplas.com.cn