类别：	聚合物 ; 热塑性聚碳酸酯（PC）
材质说明：	LNP * STAT-KON * DD0009XQ基础上，含有碳粉和阻燃聚碳酸酯是一种化合物。新增的功能包括导电，阻燃，易成型。

 

DD0009XQ LNP Stat-Kon PC 物性

Physical Properties	Metric	English	Comments
Density	1.30 g/cc	0.0470 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	SABIC Method
Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	63.0 MPa	9140 psi	5 mm/min; ISO 527
Elongation at Break	11.1 %	11.1 %	5 mm/min; ISO 527
Flexural Strength	90.0 MPa	13100 psi	break, 2 mm/min; ISO 178
Flexural Modulus	2.80 GPa	406 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	7.00 kJ/m² @Temperature 23.0 °C	3.33 ft-lb/in² @Temperature 73.4 °F	80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO)	120 kJ/m² @Temperature 23.0 °C	57.1 ft-lb/in² @Temperature 73.4 °F	80*10*4; ISO 180/1U
Electrical Properties	Metric	English	Comments
Surface Resistance	10000 - 1.00e+6 ohm	10000 - 1.00e+6 ohm	ASTM D 257
Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	60.0 µm/m-°C @Temperature 23.0 - 60.0 °C	33.3 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	63.0 µm/m-°C @Temperature 23.0 - 60.0 °C	35.0 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	132 °C	270 °F	Flatw 80*10*4 sp=64mm; ISO 75/Af
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in	UL 94

 

 

PC为非结晶性热塑性塑料

 

具高强度及弹性系数、高冲击强度、使用温度范围广

高度透明性及自由染色性

H.D.T.高

电气特性优

无味无臭对人体无害符合卫生安全

成形收缩率低、尺寸安定性良好

   

本公司以诚为信，以品质为保证，以客户满意为原则。与、我司长期代开国税17%增值税发票。

购买一吨、深圳、等东莞地区免费送货，可货到付款。不满意则可退货。欢迎广大客户、前来采购。谢谢！ 

所销售塑胶原料可提供原厂的物性表，UL MSDS SGS COC 欢迎来电咨询！ 

 

 

联系人:邓  涛　(销售经理）

联系电话:86-0769-88034082　13724501922

传    真:86-0769-88768175   QQ; 83416812 

邮    箱:13724501922@163.com

DD0009XQ LNP Stat-Kon PC

                                                                   产品价格优惠 质量保证