DP001E是聚碳酸酯基树脂含有聚四氟乙烯和硅。特点是易成型。
LNP Lubricomp PC DP001E 物性
| Physical Properties |
Metric |
English |
Comments |
| Specific Gravity |
1.20 g/cc |
1.20 g/cc |
ASTM D 792 |
| Density |
1.20 g/cc |
0.0434 lb/in³ |
ISO 1183 |
| Moisture Absorption at Equilibrium |
0.17 % |
0.17 % |
23°C / 50% RH; ISO 62 |
| |
0.12 %
@Time 86400 sec |
0.12 %
@Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow |
0.0030 - 0.0050 cm/cm
@Time 86400 sec |
0.0030 - 0.0050 in/in
@Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse |
0.0050 - 0.0070 cm/cm
@Time 86400 sec |
0.0050 - 0.0070 in/in
@Time 24.0 hour |
ASTM D 955 |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Tensile Strength at Break |
41.0 MPa |
5950 psi |
5 mm/min; ISO 527 |
| |
45.0 MPa |
6530 psi |
Type I, 5 mm/min; ASTM D 638 |
| Tensile Strength, Yield |
54.0 MPa |
7830 psi |
Type I, 5 mm/min; ASTM D 638 |
| |
54.0 MPa |
7830 psi |
5 mm/min; ISO 527 |
| Elongation at Break |
38.4 % |
38.4 % |
Type I, 5 mm/min; ASTM D 638 |
| |
48.3 % |
48.3 % |
5 mm/min; ISO 527 |
| Elongation at Yield |
6.0 % |
6.0 % |
Type I, 5 mm/min; ASTM D 638 |
| |
6.0 % |
6.0 % |
5 mm/min; ISO 527 |
| Tensile Modulus |
2.13 GPa |
309 ksi |
1 mm/min; ISO 527 |
| |
2.24 GPa |
325 ksi |
50 mm/min; ASTM D 638 |
| Flexural Strength |
72.0 MPa |
10400 psi |
ISO 178 |
| Flexural Modulus |
2.03 GPa |
294 ksi |
2 mm/min; ISO 178 |
| |
2.23 GPa |
323 ksi |
1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched |
5.95 J/cm
@Temperature 23.0 °C |
11.1 ft-lb/in
@Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched |
14.6 J/cm
@Temperature 23.0 °C |
27.4 ft-lb/in
@Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) |
36.0 kJ/m²
@Temperature 23.0 °C |
17.1 ft-lb/in²
@Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) |
181 kJ/m²
@Temperature 23.0 °C |
86.1 ft-lb/in²
@Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test |
44.0 J |
32.5 ft-lb |
Multiaxial Impact; ISO 6603 |
| |
35.0 J
@Temperature 23.0 °C |
25.8 ft-lb
@Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Coefficient of Friction, Dynamic |
0.21 |
0.21 |
ASTM D 3702 Modified |
| Coefficient of Friction, Static |
0.11 |
0.11 |
ASTM D 3702 Modified |
| K (wear) Factor |
0.000 x 10-8 mm³/N-M |
0.000 x 10-10 in³-min/ft-lb-hr |
Ring; ASTM D 3702 Modified |
| |
308 x 10-8 mm³/N-M |
153 x 10-10 in³-min/ft-lb-hr |
|
PC 应用范围
光学照明：用于制造大型灯罩、防护玻璃、
光学仪器的左右目镜筒等，还可广泛用于飞机上的透明材料。
电子电器：聚碳酸酯是优良的E（120℃）级绝缘材料，用于制造绝缘接插件、线圈框架、管座、绝缘套管、电话机壳体及零件、矿灯的电池壳等。也可用于制作尺寸精度很高的零件，如光盘、电话、电子计算机、视频录象机、电话交换器、信号继电器等通讯器材。聚碳酸酯薄摸还被广泛用作电容器、绝缘皮包、录音带、彩色录象磁带等。机械设备：用于制造各种齿轮、齿条、蜗轮、蜗杆、轴承、凸轮、螺栓、杠杆、曲轴、棘轮，也可作一些机械部件护罩、罩盖和框架等零件。医疗器材：可作医疗用途的杯、筒、瓶以及牙科器械、药品容器和手术器械，甚至还可用作人工肾、人工肺等人工脏器。其它方面：建筑上用作中空筋双壁板、暖房玻璃等；在纺织行业用作纺织纱管、纺织机轴瓦等；日用方面作奶瓶、餐具、玩具和模型等。
PC为非结晶性热塑性塑料
| 具高强度及弹性系数、高冲击强度、使用温度范围广 |
| 高度透明性及自由染色性 |
| H.D.T.高 |
| 电气特性优 |
| 无味无臭对人体无害符合卫生安全 |
| 成形收缩率低、尺寸安定性良好 |
本公司还提供、日本杜邦、德国杜邦、美国液氮、美国首诺、美国泰科纳、美国DSM、基础创新塑料（美国）、美国普立万、美国舒尔曼、美国英威达、美国RTP、德国朗盛、美国巴斯夫、上海巴斯夫、德国巴斯夫、马来西亚巴斯夫、德国弗瑞圣塔、荷兰DSM、泰国杜邦、河南神马尼龙、意大利泰克尼卡、意大利兰蒂奇、意大利LATI、上海罗地亚、法国罗地亚、日本尤尼卡、日本三菱工程、深圳东丽、日本东丽、日本旭化成、日本东洋纺织、台湾南亚、惠州南亚、台湾新光、台湾太松、日本EMS、瑞士EMS、加拿大英威达、加拿大杜邦、新加坡杜邦、新加坡美乐、基础创新塑料(美国)、基础创新塑料(日本)、基础创新塑料(泰国)、基础创新塑料(南沙)、基础创新塑料(上海)、美国杜邦、日本三菱工程.等.........
备注；塑胶原料齐全不一一介绍，更多原料请来电咨询。
| 本公司以诚为信，以品质为保证，以客户满意为原则。与、我司长期代开国税17%增值税发票。 |
| 购买一吨、深圳、等东莞地区免费送货，可货到付款。不满意则可退货。欢迎广大客户、前来采购。谢谢！ |
| 所销售塑胶原料可提供原厂的物性表，UL MSDS SGS COC 欢迎来电咨询！ |
| 联系人:邓 涛 (销售经理） |
| 联系电话:86-0769-88034082 13724501922 |
| 传 真:86-0769-88768175 QQ; 83416812 |
| 邮 箱:13724501922@163.com |
LNP Lubricomp PC DP001E
产品价格优惠 质量保证