余姚市瑞轩塑化有限公司
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 成型收缩率 | ASTM D-955 | 0.4-0.8 | % | ||
| 吸水率 | ASTM D-570 | 0.09 | % | |||
| 密度 | ASTM D-792 | 1.55 | g/cm3 | |||
| 机械性能 | 简支梁冲击强度 | 无缺口 | ISO 179 | 40 | KJ/M2 | |
| 缺口 | ISO 179 | 10 | KJ/M2 | |||
| 弯曲模量 | ASTM D-790 | 8000 | MPa | |||
| 拉伸强度 | ASTM D-638 | 120 | MPa | |||
| 伸长率 | ASTM D-638 | 4.2 | % | |||
| 弯曲强度 | ASTM D-790 | 190 | MPa | |||
| 悬臂梁缺口冲击强度 | 1/8' | ASTM D-256 | 80 | J/m | ||
| 洛氏硬度 | ASTM D-785 | 88 | M scale | |||
| 电气性能 | 体积电阻 | ASTM D-257 | 1014 | Ω.cm | ||
| 损耗因数 | ASTM D-150 | 2.5×10-2 | 106Hz | |||
| 介电强度 | 2mm | ASTM D-149 | 21 | MV/m | ||
| 介电常数 | ASTM D-150 | 3.0 | 106HZ | |||
| 热性能 | 热膨胀系数 | -30-30℃ | ASTM D-696 | 2.5 | 10-5℃mm/mm/℃ | |
| 热变形温度 | 1.82MPa | ASTM D-648 | 208 | ℃ | ||
| 其它性能 | 阻燃性 | 1/8-1/32' | UL 94 | HB | ||