宁波帝鸿塑化有限公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 燃烧性 | File No. E56070 UL&C-UL | 1/16'HB | ||
| 熔体流动速率 | 200℃×5kg | ASTM D-1238 | 4.8 | g/10min | |
| 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 52 | g/10min | |
| 比重 | ASTM D-792 | 1.03 | 23/23℃ | ||
| 机械性能 | 弯曲强度 | ASTM D-790 | 8000 | lb/in2 | |
| 弯曲强度 | ASTM D-790 | 560 | kg/cm2 | ||
| IZOD冲击强度 | 1/8' | ASTM D-256 | 5.6 | ft.lb/in | |
| IZOD冲击强度 | 1/4' | ASTM D-256 | 4.6 | ft.lb/in | |
| 引张强度 | ASTM D-638 | 4960 | kg/cm2 | ||
| IZOD冲击强度 | 1/8' | ASTM D-256 | 30 | kg/cm2 | |
| 引张强度 | ASTM D-638 | 350 | kg/cm2 | ||
| 洛氏硬度 | ASTM D-785 | 105 | R | ||
| 弯曲弹性率 | ASTM D-790 | 2.0×104 | kg/cm2 | ||
| 弯曲弹性率 | ASTM D-638 | 2.8×105 | lb/in2 | ||
| IZOD冲击强度 | 1/4' | ASTM D-256 | 25 | kg.cm/cm | |
| 伸长率 | ASTM D-638 | 30 | % | ||
| 热性能 | 热变形温度 | ASTM D-648 | 86(187) | ℉ | |
| 热变形温度 | ASTM D-648 | 96(205) | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 219 | ℉ | ||
| 维卡软化点 | ASTM D-1525 | 104 | ℃ | ||