东莞市铭远塑胶有限公司
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-1505 | 0.94 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.1 | g/10min | |
| 机械性能 | 薄膜厚度-Tested | 25.4 | um | ||
| 割线模量-1% Secant(MD) | 25.4um | ASTM D-882 | 662 | MPa | |
| 割线模量-1% Secant(TD) | 25.4um | ASTM D-882 | 855 | MPa | |
| 拉伸屈服强度(MD) | 25.4um | ASTM D-882 | 23.4 | MPa | |
| 拉伸屈服强度(TD) | 25.4um | ASTM D-882 | 27.6 | MPa | |
| 拉伸断裂强度(MD) | 25.4um | ASTM D-882 | 66.2 | MPa | |
| 拉伸断裂强度(TD) | 25.4um | ASTM D-882 | 46.2 | MPa | |
| 断裂伸长率(MD) | 25.4um | ASTM D-882 | 380 | % | |
| 断裂伸长率(TD) | 25.4um | ASTM D-882 | 620 | % | |
| 落锤冲击 | 25.4um | ASTM D-1709 | 76 | g | |
| 埃尔曼多夫撕裂强度(MD) | 25.4um | ASTM D-1922 | 16 | g | |
| 埃尔曼多夫撕裂强度(TD) | 25.4um | ASTM D-1922 | 560 | g | |