| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-1505 | 0.957 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 6.2 | g/10min | |
| 薄膜厚度 | 55.9 | μm | |||
| 机械性能 | 拉伸屈服强度(MD) | 55.9μm | ASTM D-882 | 21.7 | MPa |
| 拉伸屈服强度(TD) | 55.9μm | ASTM D-882 | 23.2 | MPa | |
| 拉伸断裂强度(TD) | 55.9μm | ASTM D-882 | 21.4 | MPa | |
| 拉伸断裂强度(MD) | 55.9μm | ASTM D-882 | 24.1 | MPa | |
| 屈服伸长率(TD) | 55.9μm | ASTM D-882 | 2 | % | |
| 屈服伸长率(MD) | 55.9μm | ASTM D-882 | 4 | % | |
| 断裂伸长率(TD) | 55.9μm | ASTM D-882 | 710 | % | |
| 断裂伸长率(MD) | 55.9μm | ASTM D-882 | 610 | % | |
| 埃尔曼多夫撕裂强度(TD) | 55.9μm | ASTM D-1922 | 110 | g | |
| 埃尔曼多夫撕裂强度(MD) | 55.9μm | ASTM D-1922 | 60 | g | |
| 热性能 | 维卡软化温度 | ASTM D-1525 | 125 | ℃ | |
| 其它性能 | 水汽传输速率 | 55.9μm,Blown Film,100% RH | ASTM F-372 | 4.3 | g/m2/24hr |