| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-1505 | 0.961 | g/cm | |
| 熔融指数 | 190℃/2.16kg | ASTM D-1238 | 3.8 | g/10min | |
| 机械性能 | 拉伸屈服强度 | ASTM D-638 | 30.8 | MPa | |
| 拉伸断裂强度 | ASTM D-638 | 26.5 | MPa | ||
| 屈服伸长率 | ASTM D-638 | 7.7 | % | ||
| 弯曲模量 | 1% Secant | ASTM D-790 | 1520 | MPa | |
| 邵氏硬度 | ASTM D-2240 | 69 | |||
| 热性能 | 热变形温度 | 0.45MPa,未退火 | ASTM D-648 | 76.1 | ℃ |
| 脆化温度 | ASTM D-746 | -76.1 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 126 | ℃ | ||