东莞市铭远塑胶有限公司
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-1505 | 0.954 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.85 | g/10min | |
| 机械性能 | 正割模量(MD) | ASTM D-882 | 931 | MPa | |
| 正割模量(TD) | ASTM D-882 | 1240 | MPa | ||
| 拉伸屈服强度(MD) | ASTM D-882 | 25.5 | MPa | ||
| 拉伸屈服强度(TD) | ASTM D-882 | 26.2 | MPa | ||
| 拉伸断裂强度(TD) | ASTM D-882 | 23.4 | MPa | ||
| 拉伸断裂强度(MD) | ASTM D-882 | 54.5 | MPa | ||
| 断裂伸长率(TD) | ASTM D-882 | 750 | % | ||
| 断裂伸长率(MD) | ASTM D-882 | 700 | % | ||
| 埃尔曼多夫撕裂强度(TD) | ASTM D-1922 | 1000 | g | ||
| 埃尔曼多夫撕裂强度(MD) | ASTM D-1922 | 32 | g | ||
| 其它性能 | 熔体温度 | 199-210 | ℃ | ||