| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-1505 | 0.949 | g/cm | |
| 熔融指数 | 190℃/2.16kg | ASTM D-1238 | 0.070 | g/10min | |
| 190℃/21.6kg | ASTM D-1238 | 16 | g/10min | ||
| 机械性能 | 拉伸屈服强度 | ASTM D-638 | 24.1 | MPa | |
| 拉伸断裂强度 | ASTM D-638 | 35.2 | MPa | ||
| 断裂伸长率 | ASTM D-638 | 630 | % | ||
| 弯曲模量 | 1% Secant | ASTM D-790 | 1100 | MPa | |
| 热性能 | 热变形温度 | 0.45MPa,未退火 | ASTM D-648 | 76 | ℃ |