SABIC? HDPE P6006
High Density Polyethylene
SABIC Americas, Inc.
产品说明：
P6006 is black compound high density (class MRS 10 - PE 100) Polyethylene with bimodal distribution of molecular mass. It is specifically designed for Pressure Pipe applications. It provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength.
Pressure pipes for drinking water, irrigation, gas distribution and waste water pipes. It is also recommended for manufacture of chemical liners and containers.
Pressure pipes for drinking water, irrigation, gas distribution and waste water pipes. It is also recommended for manufacture of chemical liners and containers.
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 1 | 0.959 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） | ISO 1133 | ||
| 190°C/21.6 kg | 6.2 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.23 | g/10 min | ISO 1133 |
| 炭黑含量 | 2.3 | % | ISO 6964 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 63 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 (2.00 mm, 模压成型) | 900 | MPa | ISO 527-2/1BA/50 |
| 拉伸应力 (屈服, 2.00 mm, 模压成型) | 23.0 | MPa | ISO 527-2/1BA/50 |
| 拉伸应变 (屈服, 2.00 mm, 模压成型) | 9.0 | % | ISO 527-2/1BA/50 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179 | ||
| -30°C | 13 | kJ/m2 | ISO 179 |
| 23°C | 26 | kJ/m2 | ISO 179 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 74.0 | °C | ISO 306 |
| 氧感应时间 (210°C) | > 20 | min | EN 728 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 熔体温度 | 190 到 220 | °C |