| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 吸水率 | 23°C,24hr | % | 1.7 | -- |
| 饱和,23°C | % | 8.0 | -- | |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | Dry｜205 | J/m |
| 23℃ | ASTM D-256 | 3.0%Water｜690 | J/m | |
| -40℃ | ASTM D-256 | Dry｜175 | J/m | |
| -40℃ | ASTM D-256 | 3.0%Water｜- | J/m | |
| IZOD无缺口冲击强度 | 23℃ | ASTM D-256 | Dry｜不断裂 | kJ/m2 |
| 23℃ | ASTM D-256 | 3.0%Water｜- | kJ/m2 | |
| 断裂伸长率 | -40℃ | ASTM D-638 | Dry｜15 | % |
| -40℃ | ASTM D-638 | 3.0%Water｜5.0 | % | |
| 23℃ | ASTM D-638 | Dry｜<200 | % | |
| 23℃ | ASTM D-638 | 3.0%Water｜<200 | % | |
| 80℃ | ASTM D-638 | Dry｜<200 | % | |
| 80℃ | ASTM D-638 | 3.0%Water｜<200 | % | |
| 拉伸屈服强度 | 80℃ | ASTM D-638 | Dry｜25 | Mpa |
| 80℃ | ASTM D-638 | 3.0%Water｜20 | Mpa | |
| 23℃ | ASTM D-638 | Dry｜60 | Mpa | |
| 23℃ | ASTM D-638 | 3.0%Water｜35 | Mpa | |
| -40℃ | ASTM D-638 | Dry｜105 | Mpa | |
| -40℃ | ASTM D-638 | 3.0%Water｜95 | Mpa | |
| 拉伸应变 | 断裂,-40°C | % | 3.5 | 1.0 |
| 断裂,23°C | % | 50 | ||
| 断裂,80°C | % | 50 | ||
| 拉伸应力 | -40°C | MPa | 105 | 95.0 |
| 23°C | MPa | 60.0 | 35.0 | |
| 80°C | MPa | 25.0 | 20.0 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | Dry｜114 | R scale |
| ASTM D785 | 114 | |||
| 23℃ | ASTM D-785 | 3.0%Water｜- | R scale | |
| 泰伯耐磨性 | 1000Cycles | mg | 6.00到7.00 | -- |
| 弯曲模量 | -40°C | MPa | 2900 | -- |
| 23°C | MPa | 2100 | 700 | |
| 80°C | MPa | 500 | -- | |
| -40℃ | ASTM D-790 | 3.0%Water｜- | GPa | |
| 23℃ | ASTM D-790 | Dry｜2.1 | GPa | |
| 23℃ | ASTM D-790 | 3.0%Water｜0.7 | GPa | |
| 80℃ | ASTM D-790 | Dry｜0.5 | GPa | |
| 80℃ | ASTM D-790 | 3.0%Water｜- | GPa | |
| -40℃ | ASTM D-790 | Dry｜2.9 | GPa | |
| 弯曲强度 | -40℃ | ASTM D-790 | Dry｜130 | Mpa |
| -40℃ | ASTM D-790 | 3.0%Water｜- | Mpa | |
| 23℃ | ASTM D-790 | Dry｜80 | Mpa | |
| 23℃ | ASTM D-790 | 3.0%Water｜- | Mpa | |
| 弯曲应力 | -40°C | MPa | 130 | -- |
| 23°C | MPa | 80.0 | -- | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 热变形温度 | 0.45MPa,未退火 | °C | 160 | -- |
| 1.8MPa,未退火 | °C | 51.0 | -- | |
| 1.86MPa | ASTM D-648 | 3.0%Water｜- | °C | |
| 0.46MPa | ASTM D-648 | Dry｜160 | °C | |
| 0.46MPa | ASTM D-648 | 3.0%Water｜- | °C | |
| 1.86MPa | ASTM D-648 | Dry｜67 | °C | |
| 熔点 | DSC | Dry｜225 | °C | |
| DSC | 3.0%Water｜- | °C | ||
| 熔融温度 | °C | 225 | -- | |
| 线形热膨胀系数 | MD | cm/cm/°C | 8.0E-5到9.0E-5 | -- |
| 线性膨胀系数 | ASTM D-696 | Dry｜8-9 | 10-5/℃ | |
| ASTM D-696 | 3.0%Water｜- | 10-5/℃ | ||
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 简支梁无缺口冲击强度 | -40°C | kJ/m2 | 16 | 54 |
| 23°C | 无断裂 | -- | ||
| 硬度 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 洛氏硬度 | R计秤,23°C | 114 | -- | |
| 物性性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 密度 | ASTM D792/ISO 1183 | 1.09 | ||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 1.7 | % | |
| 基本性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 吸水率 | 23℃ | ASTM D-570 | Dry｜8.0 | % |
| 23℃ | ASTM D-570 | 3.0%Water｜- | % | |
| 23℃，24hr | ASTM D-570 | Dry｜1.7 | % | |
| 23℃，24hr | ASTM D-570 | 3.0%Water｜- | % |