Stanyl TW200F6
30% Glass Reinforced, Heat Stabilized
Stanyl? TW200F6 is a high heat polyamide that offers excellent creep resistance, strength, stiffness and fatigue resistance,not only at ambient temperatures butespecially at high temperatures, while atthe same time providing cycle-time advantages and excellent flow.
Stanyl? TW200F6 is a high heat polyamide that offers excellent creep resistance, strength, stiffness and fatigue resistance,not only at ambient temperatures butespecially at high temperatures, while atthe same time providing cycle-time advantages and excellent flow.
| 总览 | |
| 材料状态 |
已商用：当前有效
|
| 资料1 | |
| UL 黄卡2 | |
| 搜索 UL 黄卡 | |
| 供货地区 |
北美洲
非洲和中东
拉丁美洲
欧洲
亚太地区
|
| 填料/增强材料 |
玻璃纤维增强材料, 30% 填料按重量
|
| 添加剂 |
热稳定剂
|
| 特性 |
热稳定性
|
| 加工方法 |
注射成型
|
| 多点数据 |
Isochronous Stress vs. Strain (ISO 11403)
Isothermal Stress vs. Strain (ISO 11403)
LTHA-Strain at Break vs. Time (ISO 11403)
LTHA-Stress at Break vs. Time (ISO 11403)
Secant Modulus vs. Strain (ISO 11403)
Shear Modulus vs. Temperature, Dynamic (ISO 11403)
Shear Stress vs. Shear Rate (ISO 11403)
Specific Volume vs Temperature (ISO 11403)
Tensile Fatigue
Tensile Modulus vs. Temperature (ISO 11403)
Tensile Modulus vs. Temperature, Dynamic (ISO 11403)
Viscosity vs. Shear Rate (ISO 11403)
|
| 树脂ID |
PA46-GF30
|
| 物理性能 |
干燥
|
调节后的
|
单位制
|
测试方法
|
| 密度 |
1.41
|
--
|
g/cm3
|
ISO 1183 |
| Spiral Flow | ||||
| --4 |
10.0
|
--
|
cm
|
|
| --5 |
11.0
|
--
|
cm
|
|
| --6 |
12.0
|
--
|
cm
|
|
| --7 |
3.30
|
--
|
cm
|
|
| --8 |
4.40
|
--
|
cm
|
|
| --9 |
7.60
|
--
|
cm
|
|
| 收缩率 | ISO 294-4 | |||
| 垂直 |
1.3
|
--
|
%
|
|
| 流动 |
0.50
|
--
|
%
|
|
| 吸水率 | ISO 62 | |||
| 24 hr, 23°C |
2.7
|
--
|
%
|
|
| 饱和, 23°C |
9.5
|
--
|
%
|
|
| 平衡, 23°C, 50% RH |
2.6
|
--
|
%
|
|
| 粘数 |
145
|
--
|
cm3/g
|
ISO 307 |
| 机械性能 |
干燥
|
调节后的
|
单位制
|
测试方法
|
| 拉伸模量 | ISO 527-1 | |||
| -- |
10000
|
6000
|
MPa
|
|
| -40°C |
10200
|
--
|
MPa
|
|
| 40°C |
9500
|
5300
|
MPa
|
|
| 100°C |
5500
|
--
|
MPa
|
|
| 120°C |
5300
|
--
|
MPa
|
|
| 140°C |
5100
|
--
|
MPa
|
|
| 150°C |
5000
|
--
|
MPa
|
|
| 160°C |
4750
|
--
|
MPa
|
|
| 180°C |
4550
|
--
|
MPa
|
|
| 200°C |
4300
|
--
|
MPa
|
|
| 210°C |
4200
|
--
|
MPa
|
|
| 拉伸应力 | ISO 527-2 | |||
| 断裂 |
210
|
115
|
MPa
|
|
| 断裂, -40°C |
250
|
--
|
MPa
|
|
| 断裂, 100°C |
120
|
--
|
MPa
|
|
| 断裂, 120°C |
115
|
--
|
MPa
|
|
| 断裂, 140°C |
110
|
--
|
MPa
|
|
| 断裂, 150°C |
105
|
--
|
MPa
|
|
| 断裂, 160°C |
100
|
--
|
MPa
|
|
| 断裂, 180°C |
95.0
|
--
|
MPa
|
|
| 断裂, 200°C |
90.0
|
--
|
MPa
|
|
| 断裂, 210°C |
85.0
|
--
|
MPa
|