Vydyne ECO315J NT0725) is a non-halogenated, unreinforced, flame-retardant PA66/6 co-polymer compound designed with high ductility (20% elongation), high comparative tracking index (CTI), and low corrosion for improved electrical contact performance. It is stabilized to provide heat stability up to 125°C for 1,000 hours in a dry environment. It exhibits excellent toughness and ductility, allowing increased flexibility in product design needed for living hinges and snap fits. 315J NT0725 provides enhanced flow and is lubricated for machine feed and easy mold release.
| 总览 | |
| 材料状态 |
已商用：当前有效
|
| UL 黄卡1 | |
| 搜索 UL 黄卡 | |
| 供货地区 |
北美洲
欧洲
亚太地区
|
| 添加剂 |
热稳定剂
润滑剂
阻燃性
|
| 特性 |
低密度
良好的开裂抵抗
热稳定性
韧性良好
润滑
脱模性能良好
无卤
延高的拉伸率
延展性
阻燃性
Heat Stabilized - Organic
|
| UL文件号 |
E70062
|
| 外观 |
自然色
|
| 形式 |
粒子
|
| 加工方法 |
注射成型
|
| 树脂ID |
PA66/6 FR
|
| 物理性能 |
干燥
|
调节后的
|
单位制
|
测试方法
|
| 密度 |
1.16
|
--
|
g/cm3
|
ISO 1183 |
| 收缩率 | ISO 294-4 | |||
| 垂直 : 23°C, 2.00 mm |
1.4
|
--
|
%
|
|
| 流动 : 23°C, 2.00 mm |
1.2
|
--
|
%
|
|
| 吸水率 | ISO 62 | |||
| 24 hr, 23°C |
0.80
|
--
|
%
|
|
| 平衡, 23°C, 50% RH |
2.3
|
--
|
%
|
| 机械性能 |
干燥
|
调节后的
|
单位制
|
测试方法
|
| 拉伸模量(23°C) |
3200
|
1200
|
MPa
|
ISO 527-1 |
| 拉伸应力(屈服, 23°C) |
75.0
|
42.0
|
MPa
|
ISO 527-2 |
| 拉伸应变 | ISO 527-2 | |||
| 屈服, 23°C |
3.5
|
23
|
%
|
|
| 断裂, 23°C |
22
|
140
|
%
|
|
| 弯曲模量(23°C) |
3200
|
1600
|
MPa
|
ISO 178 |
| 弯曲应力(23°C) |
92.0
|
45.0
|
MPa
|
ISO 178 |
| 泊松比(23°C) |
0.40
|
--
|
ISO 527-2 |
| 冲击性能 |
干燥
|
调节后的
|
单位制
|
测试方法
|
| 简支梁缺口冲击强度 | ISO 179/1eA | |||
| -30°C |
4.0
|
4.0
|
kJ/m2
|
|
| 23°C |
5.0
|
15
|
kJ/m2
|
|
| 简支梁无缺口冲击强度 | ISO 179/1eU | |||
| -30°C |
无断裂
|
无断裂
|
||
| 23°C |
无断裂
|
无断裂
|
||
| 悬壁梁缺口冲击强度 | ISO 180/1A | |||
| -30°C |
5.0
|
6.0
|
kJ/m2
|
|
| 23°C |
5.0
|
13
|
kJ/m2
|