Hostaform C 9021 XAP

Low Emission
POM copolymer Product with reduced emissions especially for automotive interior application. Good properties of the standard-injection molding grades like high rigidity, hardness and toughness; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation are maintained Emission according to VDA 275 10 mg/kg (natural grades) Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470 Burning rate ISO 3795 and FMVSS 302 75 mm/min for a thickness more than 1 mm. FDA = Food and Drug Administration (USA) FMVSS = Federal Motor Vehicle Safety Standard (USA)
总览
材料状态
已商用:当前有效
资料1
搜索 UL 黄卡
Automotive Specifications
供货地区
北美洲
非洲和中东
拉丁美洲
欧洲
亚太地区
添加剂
脱模
特性
低挥发
用途
汽车领域的应用
形式
粒子
加工方法
注射成型
多点数据
Creep Modulus vs. Time (ISO 11403)
Isochronous Stress vs. Strain (ISO 11403)
Isothermal Stress vs. Strain (ISO 11403)
Secant Modulus vs. Strain (ISO 11403)
Shear Modulus vs. Temperature, Dynamic (ISO 11403)
Shear Stress vs. Shear Rate (ISO 11403)
Viscosity vs. Shear Rate (ISO 11403)
物理性能
额定值
单位制
测试方法
密度
1.41
g/cm3
ISO 1183
熔融体积流量(MVR)(190°C/2.16 kg)
8.0
cm3/10min
ISO 1133
收缩率 ISO 294-4
垂直
1.9
%
流动
2.0
%
吸水率 ISO 62
饱和, 23°C, 2.00 mm
0.65
%
平衡, 23°C, 2.00 mm, 50% RH
0.20
%
机械性能
额定值
单位制
测试方法
拉伸模量
2850
MPa
ISO 527-1
拉伸应力(屈服)
64.0
MPa
ISO 527-2/50
拉伸应变(屈服)
9.0
%
ISO 527-2/50
标称拉伸断裂应变
30
%
ISO 527-2
拉伸蠕变模量 ISO 899-1
1 hr
2500
MPa
1000 hr
1300
MPa
弯曲模量
2700
MPa
ISO 178
弯曲应力
89.0
MPa
ISO 178