MLLDPE/3518CB/埃克森化学物性表
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 3.5 | g/10min | |
| 密度 | ExxonMobil Method | 0.918 | g/cm3 | ||
| 机械性能 | 屈服拉伸强度(MD) | @厚 150μ(5.9mil) | ASTM D-882 | 8 | MPa |
| 屈服拉伸强度(TD) | @厚 150μ(5.9mil) | ASTM D-882 | 8 | MPa | |
| 断裂拉伸强度(MD) | @厚 150μ(5.9mil) | ASTM D-882 | 74 | MPa | |
| 断裂拉伸强度(TD) | @厚 150μ(5.9mil) | ASTM D-882 | 47 | MPa | |
| 断裂伸长率(MD) | @厚 150μ(5.9mil) | ASTM D-882 | 510 | % | |
| 断裂伸长率(TD) | @厚 150μ(5.9mil) | ASTM D-882 | 680 | % | |
| 1%正割模量(MD) | @厚 150μ(5.9mil) | ASTM D-882 | 110 | MPa | |
| 1%正割模量(TD) | @厚 150μ(5.9mil) | ASTM D-882 | 120 | MPa | |
| 落锤冲击强度 | F50 | ASTM D-1709A | 140 | g | |
| 埃尔门多夫撕裂强度(MD) | ASTM D-1922 | 190 | g | ||
| 埃尔门多夫撕裂强度(TD) | ASTM D-1922 | 500 | g | ||
| 穿刺能力 | ExxonMobil Method | 4 | J | ||
| 热性能 | 熔体温度 | ExxonMobil Method | 114 | ℃ | |
| 其它性能 | PPA | 否 | |||
| 抗粘连剂 | 否 | ||||
| 滑爽剂 | 否 | ||||
| 热稳定剂 | 有 | ||||
| 光学性能 | 雾度 | ASTM D-1003 | 2.4 | % | |
| 光泽度 | 纵向,45° | ASTM D-2457 | 86 | ||