Braskem PE SLH118

Linear Low Density Polyethylene

Braskem

产品说明：

SLH118 is a Linear Low Density Polyethylene, copolymer of hexene-1, produced by Spherilene process. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. It contains antioxidant additives. The minimum biobased content of this grade is 84%, determined according to ASTM D6866.

物性信息：

基本信息
添加剂	抗氧化性
特性	低速凝固晶点共聚物光学性能己烯共聚单体抗氧化性可更新资源可加工性，良好良好的热封性食品接触的合规性无 BPA
用途	包装薄膜衬里管道系统混合拉伸缠绕
机构评级	ASTM D 6866 FDA 21 CFR 177.1520
加工方法	薄膜挤出吹塑薄膜

物理性能	额定值	单位制	测试方法
密度	0.916	g/cm3	ASTM D1505
熔流率（熔体流动速率）(190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	38	μm
抗张强度			ASTM D882
MD : 断裂, 38 μm, 吹塑薄膜	40.0	MPa	ASTM D882
TD : 断裂, 38 μm, 吹塑薄膜	40.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 38 μm, 吹塑薄膜	1100	%	ASTM D882
TD : 断裂, 38 μm, 吹塑薄膜	1400	%	ASTM D882
弯曲模量			ASTM D882
1% Secant, MD : 38 μm, Blown Film	200	MPa	ASTM D882
1% Secant, TD : 38 μm, Blown Film	210	MPa	ASTM D882
落锤冲击1(38 μm, 吹塑薄膜)	150	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 38 μm, 吹塑薄膜	300	g	ASTM D1922
TD : 38 μm, 吹塑薄膜	510	g	ASTM D1922

补充信息	额定值	单位制	测试方法
生物质含量	84	%	ASTM D6866

挤出	额定值	单位制
熔体温度	170 到 210	°C

备注
1 .	F50