Braskem PE SLL118/21

Linear Low Density Polyethylene

Braskem

产品说明：

SLL118/21 is a LLDPE Butene copolymer produced by Braskem. It is a general purpose product that shows a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. The minimum biobased content of this grade is 87%, determined according to ASTM D6866.

物性信息：

基本信息
添加剂	中等抗结块性中度光滑性
特性	低速凝固晶点丁烯共聚单体共聚物光学性能可更新资源可加工性，良好良好的热封性食品接触的合规性通用无 BPA 中等抗结块性中度光滑性
用途	包装薄膜衬里混合通用
机构评级	ASTM D 6866 FDA 21 CFR 177.1520
加工方法	薄膜挤出吹塑薄膜

物理性能	额定值	单位制	测试方法
密度	0.918	g/cm3	ASTM D1505
熔流率（熔体流动速率）(190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	38	μm
抗张强度			ASTM D882
MD : 断裂, 38 μm, 吹塑薄膜	40.0	MPa	ASTM D882
TD : 断裂, 38 μm, 吹塑薄膜	30.0	MPa	ASTM D882
伸长率			ASTM D882
MD : 断裂, 38 μm, 吹塑薄膜	1100	%	ASTM D882
TD : 断裂, 38 μm, 吹塑薄膜	1300	%	ASTM D882
弯曲模量			ASTM D882
1% Secant, MD : 38 μm, Blown Film	210	MPa	ASTM D882
1% Secant, TD : 38 μm, Blown Film	230	MPa	ASTM D882
落锤冲击1(38 μm, 吹塑薄膜)	130	g	ASTM D1709
埃尔曼多夫抗撕强度			ASTM D1922
MD : 38 μm, 吹塑薄膜	180	g	ASTM D1922
TD : 38 μm, 吹塑薄膜	400	g	ASTM D1922

补充信息	额定值	单位制	测试方法
生物质含量	87	%	ASTM D6866

挤出	额定值	单位制
熔体温度	180 到 210	°C

挤压说明
Blow up Ratio: from 2 to 3:1Die Gap: from 1.8 to 2.5 mmScreen Package: 40/40 - pure; 40/60/40 - BlendMass Temperature: 190°C (max 210°C)

备注
1 .	F50