LNP? THERMOCOMP? NX10302 compound 物性表
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.26 |
g/cm3 |
ASTM D792 |
| 溶化体积流率（MVR）(260°C/5.0 kg) |
14.0 |
cm3/10min |
ISO 1133 |
| 收缩率 |
|
|
ASTM D955 |
| 流动 : 24小时 |
0.60 到 0.65 |
% |
ASTM D955 |
| 横向流动 : 24小时 |
0.50 到 0.56 |
% |
ASTM D955 |
| 吸水率 |
|
|
ASTM D570 |
| 24 hr |
0.010 |
% |
ASTM D570 |
| 24 hr, 50% RH |
0.020 |
% |
ASTM D570 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量1 |
2480 |
MPa |
ASTM D638 |
| 抗张强度2 |
|
|
ASTM D638 |
| 屈服 |
46.0 |
MPa |
ASTM D638 |
| 断裂 |
47.0 |
MPa |
ASTM D638 |
| 伸长率3 |
|
|
ASTM D638 |
| 屈服 |
4.2 |
% |
ASTM D638 |
| 断裂 |
100 |
% |
ASTM D638 |
| 弯曲模量4(50.0 mm 跨距) |
2400 |
MPa |
ASTM D790 |
| 弯曲强度5 |
|
|
ASTM D790 |
| 屈服, 50.0 mm 跨距 |
80.0 |
MPa |
ASTM D790 |
| 断裂, 50.0 mm 跨距 |
79.0 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度(23°C) |
600 |
J/m |
ASTM D256 |
| 无缺口悬臂梁冲击(23°C) |
无断裂 |
|
ASTM D4812 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度(1.8 MPa, 未退火, 3.20 mm) |
108 |
°C |
ASTM D648 |
| 线形热膨胀系数 |
|
|
ASTM E831 |
| 流动 : -40 到 40°C |
8.5E-5 |
cm/cm/°C |
ASTM E831 |
| 横向 : -40 到 40°C |
9.1E-5 |
cm/cm/°C |
ASTM E831 |
| 电气性能 |
额定值 |
|
测试方法 |
| 相对电容率(1.00 GHz) |
2.74 |
|
IEC 60250 |
| 耗散因数(1.00 GHz) |
3.0E-3 |
|
IEC 60250 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
85.0 到 100 |
°C |
|
| 干燥时间 |
6.0 到 8.0 |
hr |
|
| 料筒后部温度 |
250 到 270 |
°C |
|
| 料筒中部温度 |
250 到 270 |
°C |
|
| 料筒前部温度 |
250 到 280 |
°C |
|
| 射嘴温度 |
250 到 290 |
°C |
|
| 加工（熔体）温度 |
250 到 290 |
°C |
|
| 模具温度 |
60.0 到 90.0 |
°C |
|
| 背压 |
0.300 到 0.700 |
MPa |
|
| 螺杆转速 |
40 到 70 |
rpm |
|
| 备注 |
| 1 . |
50 mm/min |
| 2 . |
类型 1, 5.0 mm/min |
| 3 . |
类型 1, 5.0 mm/min |
| 4 . |
1.3 mm/min |
| 5 . |
1.3 mm/min |