东莞市天扬塑胶原料有限公司
产品描述 Product Description
用途:电气/电子应用领域;
性能特点: 防火阻燃等级HB; 热稳定性好; Heat Stabilized,HB
填料:玻璃纤维 40
技术参数 Technical Data | |||
---|---|---|---|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
密度Density | 1.51 | g/cm3 | ISO 1183 |
收缩率Molding Shrinkage | |
ISO 294-4 | |
TDAcross Flow | 1.1 | % | ISO 294-4 |
MDFlow | 0.50 | % | ISO 294-4 |
吸水率吸水率 | |
|
|
平衡,23℃,50% RH平衡,23℃,50% RH | 2.2 | % | ISO 62 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
拉伸模量Tensile Modulus | |
ISO 527-2 | |
---- | 13000 | MPa | ISO 527-2 |
120℃120°C | 6900 | MPa | ISO 527-2 |
160℃160°C | 6100 | MPa | ISO 527-2 |
180℃180°C | 5700 | MPa | ISO 527-2 |
200℃200°C | 5300 | MPa | ISO 527-2 |
拉伸强度Tensile Stress | |
ISO 527-2 | |
断裂Break | 230 | MPa | ISO 527-2 |
断裂,120℃Break, 248°F | 130 | MPa | ISO 527-2 |
断裂,160℃Break, 320°F | 115 | MPa | ISO 527-2 |
断裂,180℃Break, 356°F | 105 | MPa | ISO 527-2 |
断裂,200℃Break, 392°F | 100 | MPa | ISO 527-2 |
拉伸应变Tensile Strain | |
ISO 527-2 | |
断裂Break | 3.0 | % | ISO 527-2 |
断裂,120℃Break, 248°F | 6.5 | % | ISO 527-2 |
断裂,160℃Break, 320°F | 6.5 | % | ISO 527-2 |
断裂,180℃Break, 356°F | 6.5 | % | ISO 527-2 |
断裂,200℃Break, 392°F | 6.5 | % | ISO 527-2 |
弯曲模量Flexural Modulus | |
ISO 178 | |
---- | 11500 | MPa | ISO 178 |
120℃120°C | 5800 | MPa | ISO 178 |
160℃160°C | 5200 | MPa | ISO 178 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
简支梁缺口冲击强度Charpy Notched Impact Strength | |
ISO 179/1eA | |
-30℃-30°C | 12 | kJ/m2 | ISO 179/1eA |
23℃23°C | 14 | kJ/m2 | ISO 179/1eA |
简支梁无缺口冲击强度Charpy Unnotched Impact Strength | |
ISO 179/1eU | |
-30℃-30°C | 75 | kJ/m2 | ISO 179/1eU |
23℃23°C | 95 | kJ/m2 | ISO 179/1eU |
悬臂梁缺口冲击强度Notched Izod Impact Strength | |
ISO 180/1A | |
-40℃-40°C | 12 | kJ/m2 | ISO 180-1A |
23℃23°C | 14 | kJ/m2 | ISO 180-1A |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
热变形温度热变形温度 | |
|
|
1.8 MPa,未退火1.8 MPa,未退火 | 290 | ℃ | ISO 75-2/A |
0.45 MPa,未退火0.45 MPa,未退火 | 290 | ℃ | ISO 75-2/B |
熔融温度Melting Temperature | 295 | ℃ | ISO 11357-3 |
线性热膨胀系数线性热膨胀系数 | |
|
|
TDTD | 5.0E-5 | 1/℃ | ISO 11359-2 |
MDMD | 2.5E-5 | 1/℃ | ISO 11359-2 |
温度指数温度指数 | |
|
|
5000 hr5000 hr | 159 | ℃ | IEC 60216 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
介电强度Electric Strength | 35 | kV/mm | IEC 60243-1 |
相对电容率Relative Permittivity | |
IEC 60250 | |
100 Hz100 Hz | 4.20 | IEC 60250 | |
1 MHz1 MHz | 4.00 | IEC 60250 | |
相比漏电起痕指数Comparative Tracking Index | 400 | V | IEC 60112 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
可燃性等级Flammability Classification | |
IEC 60695-11-10, -20 | |
0.75 mm0.75 mm | HB | IEC 60695-11-10, -20 | |
1.5 mm1.5 mm | HB | IEC 60695-11-10, -20 |
牌号简介 About |
---|
Stanyl? TE200F8是一种聚酰胺 46(尼龙 46)材料,含有的填充物为40% 玻璃纤维增强材料。 该产品在北美洲有供货,。 Stanyl? TE200F8的主要特性有: 阻燃/额定火焰 热稳定剂 Stanyl? TE200F8的典型应用领域为:电气/电子应用 40% Glass Reinforced, Heat Stabilized, for EE applications |