东莞市天扬塑胶原料有限公司
天扬销售耐高温尼龙型号齐全，微信395202604 。
产品描述 Product Description
加工条件：注射成型Injection Molding
性能特点： 无卤; 防火阻燃等级V-0; 阻燃; Halogen free,Flame Characteristics,V-0
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 1.44 | g/cm3 | ISO 1183 |
| 收缩率Molding Shrinkage | |
ISO 294-4 | |
| TDAcross Flow | 1.0 | % | ISO 294-4 |
| MDFlow | 0.30 | % | ISO 294-4 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus | 10500 | MPa | ISO 527-2 |
| 拉伸强度拉伸强度 | |
|
|
| 断裂断裂 | 150 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |
|
|
| 断裂断裂 | 2.2 | % | ISO 527-2 |
| 弯曲模量Flexural Modulus | 9000 | MPa | ISO 178 |
| 弯曲强度Flexural Stress | 230 | MPa | ISO 178 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | |
ISO 179/1eA | |
| -30℃-30°C | 7.0 | kJ/m2 | ISO 179/1eA |
| 23℃23°C | 8.0 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | |
ISO 179/1eU | |
| -30℃-30°C | 40 | kJ/m2 | ISO 179/1eU |
| 23℃23°C | 45 | kJ/m2 | ISO 179/1eU |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |
|
|
| 1.8 MPa，未退火1.8 MPa，未退火 | 283 | ℃ | ISO 75-2/A |
| 熔融温度Melting Temperature 2 2 | 310 | ℃ | ISO 11357-3 |
| 线性热膨胀系数线性热膨胀系数 | |
|
|
| TDTD | |
ISO 11359-2 | |
| ---- | 6.0E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 到 23℃-40 to 23°C | 6.0E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 到 160℃55 to 160°C | 1.0E-4 | cm/cm/℃ | ISO 11359-2 |
| MDMD | |
ISO 11359-2 | |
| ---- | 2.0E-5 | cm/cm/℃ | ISO 11359-2 |
| -40 到 23℃-40 to 23°C | 2.0E-5 | cm/cm/℃ | ISO 11359-2 |
| 55 到 160℃55 to 160°C | 2.0E-5 | cm/cm/℃ | ISO 11359-2 |
| 相对温度指数相对温度指数 | |
|
|
| 电气性能电气性能 | |
UL 746 | |
| 0.40 mm0.40 mm | 140 | ℃ | UL 746 |
| 0.75 mm0.75 mm | 140 | ℃ | UL 746 |
| 1.5 mm1.5 mm | 140 | ℃ | UL 746 |
| 3.0 mm3.0 mm | 140 | ℃ | UL 746 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度Electric Strength | 36 | kV/mm | IEC 60243-1 |
| 相对电容率Relative Permittivity | |
IEC 60250 | |
| 100 Hz100 Hz | 4.10 | IEC 60250 | |
| 1 MHz1 MHz | 3.90 | IEC 60250 | |
| 耗散因数Dissipation Factor | |
IEC 60250 | |
| 100 Hz100 Hz | 6.5E-3 | IEC 60250 | |
| 1 MHz1 MHz | 0.012 | IEC 60250 | |
| 相比漏电起痕指数Comparative Tracking Index | 600 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | |
UL 94 | |
| 0.75 mm0.75 mm | V-0 | UL 94 | |
| 1.50 mm1.5 mm | V-0 | UL 94 | |
| 可燃性等级Flammability Classification | |
IEC 60695-11-10, -20 | |
| 0.75 mm0.75 mm | V-0 | IEC 60695-11-10, -20 | |
| 1.5 mm1.5 mm | V-0 | IEC 60695-11-10, -20 | |
| 灼热丝起燃温度Glow Wire Ignition Temperature | |
IEC 60695-2-13 | |
| 0.4 mm0.40 mm | 700 | ℃ | IEC 60695-2-13 |
| 0.75 mm0.75 mm | 725 | ℃ | IEC 60695-2-13 |
| 3 mm3.0 mm | 800 | ℃ | IEC 60695-2-13 |
| 极限氧指数Oxygen Index | 37 | % | ISO 4589-2 |
| FMVSS 阻燃等级FMVSS Flammability | DNI | FMVSS 302 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| OdorOdor | 3.50 | VDA 270 | |
| 牌号简介 About |
|---|
| 30%玻璃纤维增强，阻燃，非卤化，ppa，高性能聚酰胺 30% Glass Reinforced, Flame Retardant, Non-Halogenated, PPA, High Performance Polyamide |