| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 0.96 | ||
| 成型收缩率 | ASTM D-955 | 1.1-1.5 | % | ||
| 机械性能 | 拉伸屈服强度 | ASTM D-638 | 350 | Kg./cm2 | |
| 弯曲强度 | ASTM D-790 | 6100 | psi | ||
| 拉伸屈服强度 | ASTM D-638 | 34 | MPa | ||
| 拉伸屈服强度 | ASTM D-638 | 50000 | psi | ||
| 弯曲模量 | ASTM 790 | 1770 | MPa | ||
| 弯曲强度 | ASTM D-790 | 42 | MPa | ||
| Izod缺口冲击强度 | ASTM D-256 | 7 | Kg.cm/cm | ||
| 弯曲强度 | ASTM D-790 | 430 | Kg./cm2 | ||
| 弯曲模量 | ASTM D-790 | 18000 | Kg./cm2 | ||
| 弯曲模量 | ASTM D-790 | 260 | psi | ||
| Izod缺口冲击强度 | ASTM D-256 | 70 | J/m | ||
| 断裂伸长率 | ASTM D-638 | 60 | % | ||
| Izod缺口冲击强度 | ASTM D-256 | 1.3 | ft.lb/in | ||
| 热性能 | 热变形温度 | 1.82Mpa | ASTM D-648 | 165 | °F |
| 耐燃性 | ASTM D-UL94 | HB | class | ||
| 热变形温度 | 0.45Mpa | ASTM D-648 | 265 | °F | |
| 热变形温度 | 1.82Mpa | ASTM D-648 | 73 | ℃ | |
| 热变形温度 | 0.45Mpa | ASTM D-648 | 130 | ℃ | |