| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.22 | ||
| 成型收缩率 | ASTM D-955 | 0.6-1.0 | % | ||
| 机械性能 | 弯曲模量 | ASTM D-790 | 34000 | Kg/cm2 | |
| 弯曲强度 | ASTM D-790 | 400 | Kg/cm2 | ||
| 拉伸屈服强度 | ASTM D-638 | 27 | MPa | ||
| 断裂伸长率 | ASTM D-638 | 15 | % | ||
| 弯曲模量 | ASTM 790 | 3330 | MPa | ||
| 弯曲模量 | ASTM D-256 | 0.6 | ft.lb/in | ||
| 拉伸屈服强度 | ASTM D-638 | 3800 | psi | ||
| 弯曲强度 | ASTM D-790 | 5700 | psi | ||
| 拉伸屈服强度 | ASTM D-638 | 270 | Kg/cm2 | ||
| 弯曲模量 | ASTM D-256 | 30 | J/m | ||
| 弯曲强度 | ASTM D-790 | 39 | MPa | ||
| Izod缺口冲击强度 | ASTM D-256 | 3 | Kg.cm/cm | ||
| 弯曲模量 | ASTM D-790 | 480 | psi | ||
| 热性能 | 热变形温度 | 0.45Mpa | ASTM D-648 | 145 | ℃ |
| 热变形温度 | 1.82Mpa | ASTM D-648 | 210 | °F | |
| 热变形温度 | 1.82Mpa | ASTM D-648 | 100 | ℃ | |
| 热变形温度 | 0.45Mpa | ASTM D-648 | 295 | °F | |
| 耐燃性 | ASTM D-UL94 | HB | class | ||