东莞市程锦塑化有限公司
耐高温POM 美国杜邦988P产品说明:
加工改进的高粘度均聚缩醛
耐高温POM 美国杜邦988P物性参数表:
物性表
物性纠错
物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
---|---|---|---|---|
模缩率 | 1.8-2.0 | % | ||
机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
埃佐冲击试验 | 缺口-40℃ | ASTM D-256 | 55 | J/m |
23℃ | ASTM D-256 | 71 | J/m | |
无缺口23℃ | ASTM D-256 | 1620 | J/m | |
弹性系数 | 23℃ | ASTM D-638 | 3640 | Mpa |
负载变形量 | 140kg/cm2,50℃ | ASTM D-621 | 0.5 | % |
抗剪强度 | 23℃ | ASTM D-732 | 66 | Mpa |
抗拉伸冲击强度 | 23℃ | ASTM D-1822 | 250 | kJ/m2 |
拉伸强度 | -55℃ | ASTM D-638 | 101 | Mpa |
100℃ | ASTM D-638 | 36 | Mpa | |
23℃ | ASTM D-638 | 69 | Mpa | |
70℃ | ASTM D-638 | 48 | Mpa | |
122℃ | ASTM D-638 | 26 | Mpa | |
洛氏硬度M | ASTM D-785 | 94 | ||
洛氏硬度R | ASTM D-785 | 120 | ||
挠曲变形强度 | 23℃ | ASTM D-790 | 97 | Mpa |
挠曲疲劳忍耐限度 | 50%RH,23℃,106周期 | ASTM D-671 | 32 | Mpa |
挠曲系数 | 122℃ | ASTM D-790 | 755 | Mpa |
-55℃ | ASTM D-790 | 4730 | Mpa | |
70℃ | ASTM D-790 | 1720 | Mpa | |
100℃ | ASTM D-790 | 1030 | Mpa | |
23℃ | ASTM D-790 | 3220 | Mpa | |
破裂点拉伸变形量 | 100℃ | ASTM D-638 | 260 | % |
122℃ | ASTM D-638 | 260 | % | |
-55℃ | ASTM D-638 | 10 | % | |
23℃ | ASTM D-638 | 25 | % | |
70℃ | ASTM D-638 | 180 | % | |
压缩应力 | 23℃,10%变形 | ASTM D-695 | 121 | Mpa |
23℃,1%变形 | ASTM D-695 | 35 | Mpa | |
热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
热传导系数 | 0.37 | w/mk | ||
热畸变温度 | 1.8MPa | ASTM D-648 | 136 | |
熔点 | ASTM D-2133 | 175 | ||
线性热膨胀系数 | 104-160℃ | ASTM D-696 | 14.9 | 10-5m/m |
60-104℃ | ASTM D-696 | 13.7 | 10-5m/m | |
29-60℃ | ASTM D-696 | 12.2 | 10-5m/m | |
-40-29 | ASTM D-696 | 10.4 | 10-5m/m | |
自燃性 | UL 94 | HB | ||
电气性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
介电常数 | 50%RH,23℃,102-106Hz | ASTM D-150 | 3.7 | ohm-cm |
介电强度 | 2.3mm | ASTM D-149 | 19.7 | KV/mm |
介电因数 | 50%RH,23℃,106Hz | ASTM D-150 | 0.005 | |
抗电弧 | 3.1mm | ASTM D-495 | 220 | sec |
容积电阻率 | 23℃,0.2%含水量 | ASTM D-257 | ≥14.9 | ohm-cm |
基本性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
吸水率 | 50%相对湿度 | ASTM D-570 | 0.22 | % |
浸渍平衡点 | ASTM D-570 | 0.90 | % | |
24小时浸渍 | ASTM D-570 | 0.25 | % |