DuPont Delrin? 500AL NC010 Acetal(聚甲醛-POM原料)
The property table is provided bywww.cn-plas.com,welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Specific Gravity密度
|
1.39g/cc
|
1.39g/cc
|
ASTM D792
|
|
Density
|
1.39g/cc
|
0.0502lb/in3
|
ISO 1183
|
|
Linear Mold Shrinkage线性收缩率
|
0.017-0.020cm/cm
@Thickness 3.20 mm |
0.017-0.020in/in
@Thickness 0.126 in |
Flow, 24h; ASTM D955
|
|
0.017-0.020cm/cm
@Thickness 3.20 mm |
0.017-0.020in/in
@Thickness 0.126 in |
Transverse, 24h; ASTM D955
|
|
|
Linear Mold Shrinkage, Flow线性收缩率/流动
|
0.018cm/cm
@Thickness 2.00 mm |
0.018in/in
@Thickness 0.0787 in |
Parallel; ISO 294-4
|
|
0.019cm/cm
@Thickness 4.00 mm |
0.019in/in
@Thickness 0.157 in |
Parallel; ISO 294-4
|
|
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.017cm/cm
@Thickness 2.00 mm |
0.017in/in
@Thickness 0.0787 in |
Normal; ISO 294-4
|
|
0.019cm/cm
@Thickness 4.00 mm |
0.019in/in
@Thickness 0.157 in |
Normal; ISO 294-4
|
|
|
Melt Flow熔体流动速率
|
6.0g/10 min
@Load 1.05 kg, Temperature 190 °C |
6.0g/10 min
@Load 2.31 lb, Temperature 374 °F |
ASTM D1238
|
|
14g/10 min
@Load 2.16 kg, Temperature 190 °C |
14g/10 min
@Load 4.76 lb, Temperature 374 °F |
ISO 1133
|
|
|
Melt Index of Compound
|
12g/10 min
@Load 2.16 kg, Temperature 190 °C |
12g/10 min
@Load 4.76 lb, Temperature 374 °F |
cm3/10 min; ISO 1133
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Tensile Strength拉伸强度
|
66.0MPa
@Temperature 23.0 °C |
9570psi
@Temperature 73.4 °F |
5mm/min (0.2in/min); ASTM D638
|
|
Tensile Strength, Yield屈服拉伸强度
|
65.0MPa
@Temperature 23.0 °C |
9430psi
@Temperature 73.4 °F |
ISO 527
|
|
66.0MPa
@Temperature 23.0 °C |
9570psi
@Temperature 73.4 °F |
5mm/min (0.2in/min); ASTM D638
|
|