东莞市樟木头宇涛塑胶原料经营部
杜邦PA66 增强级70G13L 高温尼龙70G43L
特性?：玻纤增强;高强度;高刚性;耐高温
应用领域?：电气领域;电子领域;汽车领域;健身器材;体育用品;电器用具
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 密度 / 比重 | ASTM D-792 | 1.22 | ||
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 埃佐冲击强度 | 23℃,DAM | ASTM D-256 | 48 | J/m |
| 23℃,50%RH | ASTM D-256 | 53 | J/m | |
| 断裂伸长率 | 23℃,50%RH | ASTM D-638 | 8 | % |
| ASTM D638/ISO 527 | 2 | % | ||
| 23℃,DAM | ASTM D-638 | 2 | % | |
| 挤剪强度 | 23℃,DAM | ASTM D-732 | 76 | Mpa |
| 拉伸强度 | 23℃,50%RH | ASTM D-638 | 82.7 | Mpa |
| 23℃,DAM | ASTM D-638 | 103.4 | Mpa | |
| ASTM D638/ISO 527 | 103.4 | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度M | 50%RH | ASTM D-785 | M84 | |
| DAM | ASTM D-785 | M95 | ||
| 洛氏硬度R | DAM | ASTM D-785 | R122 | |
| 50%RH | ASTM D-785 | R113 | ||
| 挠曲模量 | 23℃,50%RH | ASTM D-790 | 2758 | Mpa |
| 23℃,DAM | ASTM D-790 | 4826 | Mpa | |
| 挠曲强度 | 23℃,DAM | ASTM D-790 | 165 | Mpa |
| 泰伯磨耗量 | 50%RH | 12 | cycles | |
| 弯曲模量 | ASTM D790/ISO 178 | 4826 | kg·cm/cm(J/M)ft·lb/in | |
| 弯曲强度 | ASTM D790/ISO 178 | 165 | kg·cm/cm(J/M)ft·lb/in | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 燃烧性（率） | UL94 | HB | ||
| 热畸变温度 | 1.8MPa | ASTM D-648 | 243 | ℃ |
| 熔点 | 255 | ℃（℉） | ||
| 50%RH | ASTM D-789 | 255 | ℃ | |
| DAM | ASTM D-789 | 255 | ℃ | |
| 线性膨胀系数 | ASTM D696/ISO 11359 | 2.7×10-5 | mm/mm.℃ | |
| 线性热膨胀系数 | ASTM D-696 | 2.7×10 | m/m/℃ | |
| 电气性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 介电常数 | ASTM D150/IEC 60250 | 130 | ||
| ASTM D150/IEC 60250 | 150 | |||
| 物性性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 比重（密度） | ASTM D792/ISO 1183 | 1.22 |