东莞市樟木头宇涛塑胶原料经营部
深圳杜邦pa66 70G33L增强级尼龙
材料的性能表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 密度 ?? | ASTM D-792 | 1.38 | ||
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 埃佐冲击强度 | 23℃,50%RH | ASTM D-256 | 133 | J/m |
| 23℃,DAM | ASTM D-256 | 107 | J/m | |
| 断裂伸长率 | 23℃,DAM | ASTM D-638 | 3 | % |
| ASTM D638/ISO 527 | 3.5 | % | ||
| 23℃,50%RH | ASTM D-638 | 4 | % | |
| 挤剪强度 | 23℃,DAM | ASTM D-732 | 86 | Mpa |
| 拉伸模量 | ASTM D638/ISO 527 | 10500 | kg/cm2(MPa)[Lb/in2] | |
| 拉伸强度 | ASTM D638/ISO 527 | 200 | kg/cm2(MPa)[Lb/in2] | |
| 23℃,50%RH | ASTM D-638 | 124.1 | Mpa | |
| 23℃,DAM | ASTM D-638 | 196.1 | Mpa | |
| 洛氏硬度M | DAM | ASTM D-785 | M101 | |
| 挠曲模量 | 23℃,DAM | ASTM D-790 | 8963 | |
| 23℃,50%RH | ASTM D-790 | 6205 | Mpa | |
| 挠曲强度 | 23℃,DAM | ASTM D-790 | 262 | Mpa |
| 泰伯磨耗量 | 50%RH | 14 | cycles | |
| 弯曲模量 | ASTM D790/ISO 178 | 9300 | kg·cm/cm(J/M)ft·lb/in | |
| 弯曲强度 | ASTM D790/ISO 178 | 290 | kg·cm/cm(J/M)ft·lb/in | |
| Charpy冲击强度 | ASTM D256/ISO 179 | 85 100 | kg·cm/cm(J/M)ft·lb/in | |
| IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 13 17 | kg·cm/cm(J/M)ft·lb/in | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 热变形温度 | ASTM D648/ISO 75 | 252 | ℃（℉） | |
| ASTM D648/ISO 75 | 261 | ℃（℉） | ||
| 热畸变温度 | 1.8MPa | ASTM D-648 | 249 | ℃ |
| 熔点 | DAM | ASTM D-789 | 255 | ℃ |
| 50%RH | ASTM D-789 | 255 | ℃ | |
| 线性膨胀系数 | ASTM D696/ISO 11359 | 0.83 | mm/mm.℃ | |
| 线性热膨胀系数 ?? | ASTM D-696 | 2.3×10 | m/m/℃ | |
| 电气性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 介电常数 | DAM@10 | ASTM D-150 | 3.7 | |
| DAM@10 | ASTM D-150 | 4.5 | ||
| 100%RH@10 | ASTM D-150 | 10.7 | ||
| 100%RH@10 | ASTM D-150 | 25.0 |