东莞市樟木头宇涛塑胶原料经营部
杜邦PA66 101L注射成型
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
|---|---|---|---|---|
| 密度 / 比重 | ASTM D-792 | DAM｜1.14 | ||
| ASTM D-792 | 50%RH｜1.14 | |||
| 泰伯磨耗量 | cs-17 Wheel,1000g | DAM｜- | mg/1000 cycles | |
| cs-17 Wheel,1000g | 50%RH｜7 | mg/1000 cycles | ||
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 单位 |
| 1%形变时的压应力 | ASTM D-695 | DAM｜33.8 | Mpa | |
| ASTM D-695 | 50%RH｜- | Mpa | ||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | DAM｜53 | J/m |
| 23℃ | ASTM D-256 | 50%RH｜112 | J/m | |
| 断裂伸长率 | ASTM D638/ISO 527 | 60 | % | |
| 23℃ | ASTM D-638 | DAM｜60 | % | |
| 23℃ | ASTM D-638 | 50%RH｜≥300 | % | |
| 剪切强度 | 23℃ | ASTM D-732 | DAM｜66.2 | Mpa |
| 23℃ | ASTM D-732 | 50%RH｜- | Mpa | |
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | DAM｜157 | kJ/m2 |
| 短试样23℃ | ASTM D-1822 | 50%RH｜231 | kJ/m2 | |
| 长试样23℃ | ASTM D-1822 | DAM｜504 | kJ/m2 | |
| 长试样23℃ | ASTM D-1822 | 50%RH｜1470 | kJ/m2 | |
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜82.7 | Mpa |
| 23℃ | ASTM D-638 | 50%RH｜77.2 | Mpa | |
| ASTM D638/ISO 527 | 82.7 | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度M | ASTM D-785 | DAM｜M79 | ||
| ASTM D-785 | 50%RH｜M59 | |||
| 洛氏硬度R | ASTM D-785 | DAM｜R121 | ||
| ASTM D-785 | 50%RH｜R108 | |||
| 屈服强度 | 23℃ | DAM｜82.7 | Mpa | |
| 23℃ | 50%RH｜58.6 | Mpa | ||
| 屈服伸长率 | ASTM D-638 | DAM｜5 | % | |
| ASTM D-638 | 50%RH｜25 | % | ||
| 揉曲模量 | 23℃ | ASTM D-790 | DAM｜2827 | Mpa |
| 23℃ | ASTM D-790 | 50%RH｜1207 | Mpa | |
| 伸长率 | ASTM D638/ISO 527 | 82.7 | % | |
| 硬度计硬度 | ASTM D-676 | DAM｜89 | ||
| ASTM D-676 | 50%RH｜82 |