Plexiglas? DRM2-101
Polymethyl Methacrylate Acrylic
Altuglas International of Arkema Inc.
产品说明:
Plexiglas? DRM2-101 is an impact modified thermoplastic acrylic resin formulated for injection molding and extrusion applications. It has a matte appearance, is heat resistance and provides 10 times the impact resistance of standard acrylics. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics.
物性信息:
基本信息 | |
---|---|
添加剂 |
|
特性 |
|
用途 |
|
机构评级 |
|
RoHS 合规性 |
|
外观 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
比重 | 1.15 | g/cm3 | ASTM D792 |
熔流率(熔体流动速率) (230°C/3.8 kg) | 1.0 | g/10 min | ASTM D1238 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
悬壁梁缺口冲击强度 (23°C) | 43 | J/m | ASTM D256 |
光学性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
透射率 (3180 μm) | 88.0 | % | ASTM D1003 |
雾度 (3180 μm) | 2.5 | % | ASTM D1003 |
注射 | 额定值 | 单位制 | |
---|---|---|---|
干燥温度 | 82.2 到 87.8 | °C | |
干燥时间 | 4.0 | hr | |
建议的最大水分含量 | 0.10 | % | |
建议注射量 | 50 | % | |
建议的最大回制料比例 | 20 | % | |
料筒后部温度 | 227 | °C | |
料筒中部温度 | 232 | °C | |
料筒前部温度 | 238 | °C | |
射嘴温度 | 232 | °C | |
加工(熔体)温度 | 271 | °C | |
模具温度 | 37.8 到 87.8 | °C | |
注射速度 | 中等 | |
|
背压 | 0.689 | MPa | |
螺杆转速 | 50 到 100 | rpm | |
螺杆长径比 | 15.0:1.0到20.0:1.0 | |
|
螺杆压缩比 | 2.0:1.0 至 2.5:1.0 | |
|
排气孔深度 | 0.051 | mm |