陶氏高密度聚乙烯 DMDA-8907 NT 7
High Density Polyethylene Resin
产品说明:
DOW DMDA-8907 NT 7 High Density Polyethylene (HDPE) Resin is produced via UNIPOL? Process Technology from Dow and is intended for use in injection molding applications such as pails, industrial parts and other shipping containers. This resin has been designed to provide excellent processability for molders and to meet the rigorous performance characteristics of applications requiring stackability, environmental stress crack resistance and impact strength.
Complies with:
- Injection molding
- For injection molded pails, industrial parts and other shipping containers
- Excellent impact strength, stress crack resistance and processability
- Very narrow molecular weight distribution
Complies with:
- U.S. FDA 21 CFR 177.1520 (c)3.2a
- Canadian HPFB No Objection
- EU, No 10/2011
- U.S. USP
U.S. FDA DMF
DOW DMDA-8907 NT 7 高密度聚乙烯 (HDPE) 树脂通过陶氏的 UNIPOL? 工艺技术生产，旨在用于注塑成型应用，例如桶、工业零件和其他运输容器。该树脂旨在为成型商提供出色的加工性能，并满足要求可堆叠性、耐环境应力开裂性和冲击强度的应用的严格性能特征。注塑成型 用于注塑成型的桶、工业部件和其他运输容器 出色的冲击强度、抗应力开裂性和可加工性 非常窄的分子量分布 符合：美国 FDA 21 CFR 177.1520 (c)3.2a 加拿大 HPFB 无异议 EU, No 10/2011美国 USP 美国 FDA DMF。
|
添加剂
|
|
|||
|
机构评级
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
0.952
|
g/cm3
|
ASTM D792 |
|
熔流率（熔体流动速率）(190°C/2.16 kg)
|
6.8
|
g/10 min
|
ASTM D1238 |
|
抗环境应力开裂(50°C, 100% Igepal, F50)
|
12.0
|
hr
|
ASTM D1693 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
肖氏硬度(邵氏 D)
|
59
|
ASTM D2240 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
抗张强度
|
ASTM D638 | ||
|
屈服
|
26.9
|
MPa
|
|
|
断裂
|
22.8
|
MPa
|
|
|
伸长率
|
ASTM D638 | ||
|
屈服
|
7.0
|
%
|
|
|
断裂
|
1100
|
%
|
|
|
弯曲模量 - 2% 正割
|
1070
|
MPa
|
ASTM D790B |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸冲击强度2
|
84.1
|
kJ/m2
|
ASTM D1822 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度(0.45 MPa, 未退火)
|
72.8
|
°C
|
ASTM D648 |
|
脆化温度
|
-76.1
|
°C
|
ASTM D746 |
|
维卡软化温度
|
128
|
°C
|
ASTM D1525 |
|
溶融温度（DSC）
|
131
|
°C
|
内部方法 |
|
结晶峰温度 (DSC)
|
118
|
°C
|
内部方法 |