上海正逢塑胶有限公司
基础创新 ULTEM? Filament AM9085F
王经理：13913231960
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
1.28
|
g/cm3
|
ASTM D792 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
ASTM D638 | ||
|
XY Orientation
|
2180
|
MPa
|
|
|
XZ Orientation
|
2560
|
MPa
|
|
|
ZX Orientation
|
2440
|
MPa
|
|
|
抗张强度2
|
ASTM D638 | ||
|
XY Orientation : 断裂
|
62.0
|
MPa
|
|
|
XZ Orientation : 断裂
|
80.0
|
MPa
|
|
|
ZX Orientation : 断裂
|
45.0
|
MPa
|
|
|
伸长率2
|
ASTM D638 | ||
|
XY Orientation : 断裂
|
5.1
|
%
|
|
|
XZ Orientation : 断裂
|
5.8
|
%
|
|
|
ZX Orientation : 断裂
|
2.3
|
%
|
|
|
弯曲模量3
|
ASTM D790 | ||
|
XY Orientation
|
2130
|
MPa
|
|
|
XZ Orientation
|
2550
|
MPa
|
|
|
ZX Orientation
|
2070
|
MPa
|
|
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度4
|
ASTM D256 | ||
|
XY Orientation : 23°C
|
100
|
J/m
|
|
|
XZ Orientation : 23°C
|
100
|
J/m
|
|
|
ZX Orientation : 23°C
|
33
|
J/m
|
|
|
无缺口悬臂梁冲击
|
ASTM D4812 | ||
|
XY Orientation : 23°C
|
760
|
J/m
|
|
|
XZ Orientation : 23°C
|
1000
|
J/m
|
|
|
ZX Orientation : 23°C
|
130
|
J/m
|
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
ASTM D648 | ||
|
XY Orientation : 1.8 MPa, 未退火, 3.20 mm
|
175
|
°C
|
|
|
XZ Orientation : 1.8 MPa, 未退火, 3.20 mm
|
175
|
°C
|
|
|
ZX Orientation : 1.8 MPa, 未退火, 3.20 mm
|
165
|
°C
|
|
|
线形热膨胀系数
|
ASTM E831 | ||
|
流动, XY Orientation
|
5.7E-5
|
cm/cm/°C
|
|
|
流动, XZ Orientation
|
6.1E-5
|
cm/cm/°C
|
|
|
流动, ZX Orientation
|
6.2E-5
|
cm/cm/°C
|
|
|
垂直, XY Orientation
|
5.8E-5
|
cm/cm/°C
|
|
|
垂直, XZ Orientation
|
6.1E-5
|
cm/cm/°C
|
|
|
垂直, ZX Orientation
|
6.3E-5
|
cm/cm/°C
|
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
ASTM D257 | ||
|
XY Orientation
|
1.1E+15
|
ohms·cm
|
|
|
XZ Orientation
|
1.1E+15
|
ohms·cm
|
|
|
介电常数
|
ASTM D150 | ||
|
XY Orientation : 100 MHz
|
2.54
|
||
|
XZ Orientation : 100 MHz
|
2.73
|
||
|
XY Orientation : 500 MHz
|
2.53
|
||
|
XZ Orientation : 500 MHz
|
2.72
|
||
|
XY Orientation : 1.00 GHz
|
2.52
|
||
|
XZ Orientation : 1.00 GHz
|
2.71
|
||
|
耗散因数
|
ASTM D150 | ||
|
XY Orientation : 100 MHz
|
2.3E-3
|
||
|
XZ Orientation : 100 MHz
|
3.0E-3
|
||
|
XY Orientation : 500 MHz
|
5.0E-3
|
||
|
XZ Orientation : 500 MHz
|
5.7E-3
|
||
|
XY Orientation : 1.00 GHz
|
4.0E-3
|
||
|
XZ Orientation : 1.00 GHz
|
4.0E-3
|
||
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级5
|
UL 94 | ||
|
XY Orientation : 1.5 mm
|
V-0
|
||
|
XZ Orientation : 1.5 mm
|
V-0
|
||
|
ZX Orientation : 1.5 mm
|
V-0
|
||
|
XY Orientation : 3.0 mm
|
V-0
|
||
|
XZ Orientation : 3.0 mm
|
V-0
|
||
|
ZX Orientation : 3.0 mm
|
V-0
|
||
|
FAA Flammability6(1.50 mm)
|
PASS
|
FAR 25.853 | |
|
OSU峰值放热速率 - 5 minute test6(1.50 mm)
|
45.0
|
kW/m2
|
FAR 25.853 |
|
OSU总放热量 - 2 minute test6(1.50 mm)
|
44.0
|
kW·min/m2
|
FAR 25.853 |