基础创新 ULTEM? Filament AM1010F
王经理：13913231960
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
密度 / 比重
|
1.28
|
g/cm3
|
ASTM D792 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
ASTM D638 | ||
|
XY Orientation
|
2750
|
MPa
|
|
|
XZ Orientation
|
2870
|
MPa
|
|
|
ZX Orientation
|
2840
|
MPa
|
|
|
抗张强度1
|
ASTM D638 | ||
|
XY Orientation : 断裂
|
73.0
|
MPa
|
|
|
XZ Orientation : 断裂
|
80.0
|
MPa
|
|
|
ZX Orientation : 断裂
|
34.0
|
MPa
|
|
|
伸长率1
|
ASTM D638 | ||
|
XY Orientation : 断裂
|
4.0
|
%
|
|
|
XZ Orientation : 断裂
|
3.8
|
%
|
|
|
ZX Orientation : 断裂
|
1.3
|
%
|
|
|
弯曲模量2
|
ASTM D790 | ||
|
XY Orientation
|
2520
|
MPa
|
|
|
XZ Orientation
|
2840
|
MPa
|
|
|
ZX Orientation
|
2380
|
MPa
|
|
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度
|
ASTM D256 | ||
|
XY Orientation : 23°C
|
31
|
J/m
|
|
|
XZ Orientation : 23°C
|
37
|
J/m
|
|
|
ZX Orientation : 23°C
|
30
|
J/m
|
|
|
无缺口悬臂梁冲击
|
ASTM D4812 | ||
|
XY Orientation : 23°C
|
270
|
J/m
|
|
|
XZ Orientation : 23°C
|
240
|
J/m
|
|
|
ZX Orientation : 23°C
|
130
|
J/m
|
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
ASTM D648 | ||
|
XY Orientation : 1.8 MPa, 未退火, 3.20 mm
|
211
|
°C
|
|
|
XZ Orientation : 1.8 MPa, 未退火, 3.20 mm
|
210
|
°C
|
|
|
ZX Orientation : 1.8 MPa, 未退火, 3.20 mm
|
208
|
°C
|
|
|
维卡软化温度
|
ASTM D15253 | ||
|
XY Orientation
|
220
|
°C
|
|
|
XZ Orientation
|
220
|
°C
|
|
|
ZX Orientation
|
220
|
°C
|
|
|
线形热膨胀系数
|
ASTM E831 | ||
|
流动, XY Orientation
|
5.1E-5
|
cm/cm/°C
|
|
|
流动, XZ Orientation
|
5.3E-5
|
cm/cm/°C
|
|
|
流动, ZX Orientation
|
5.3E-5
|
cm/cm/°C
|
|
|
垂直, XZ Orientation
|
5.2E-5
|
cm/cm/°C
|
|
|
垂直, XY Orientation
|
5.3E-5
|
cm/cm/°C
|
|
|
垂直, ZX Orientation
|
5.3E-5
|
cm/cm/°C
|
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
体积电阻率
|
ASTM D257 | ||
|
XY Orientation
|
6.2E+14
|
ohms·cm
|
|
|
XZ Orientation
|
1.3E+15
|
ohms·cm
|
|
|
介电常数
|
ASTM D150 | ||
|
XY Orientation : 1.90 GHz
|
2.90
|
||
|
XZ Orientation : 1.90 GHz
|
2.90
|
||
|
耗散因数
|
ASTM D150 | ||
|
XY Orientation : 1.90 GHz
|
3.0E-3
|
||
|
XZ Orientation : 1.90 GHz
|
3.0E-3
|
||
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级4
|
UL 94 | ||
|
XY Orientation : 1.5 mm
|
V-0
|
||
|
XZ Orientation : 1.5 mm
|
V-0
|
||
|
ZX Orientation : 1.5 mm
|
V-0
|
||
|
XY Orientation : 3.0 mm
|
5VA
|
||
|
FAA Flammability5(1.50 mm)
|
Passed
|
FAR 25.853 | |
|
OSU峰值放热速率 - 5 minute test5(1.50 mm)
|
23.0
|
kW/m2
|
FAR 25.853 |
|
OSU总放热量 - 2 minute test5(1.50 mm)
|
5.00
|
kW·min/m2
|
FAR 25.853 |
|
Vertical Burn5
|
FAR 25.853 | ||
|
12s, passes at : 1.50 mm
|
0.0
|
sec
|
|
|
60s, passes at : 1.50 mm
|
2.0
|
sec
|