东莞市宏阔塑胶有限公司
EMS-Grivory Grivory? GVX-5 H black 9915
Nylon
EMS-Grivory (EMS-CHEMIE)
产品说明：
Product description: Grivory GVX-5H black 9915 is a 50% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyamide. Grivory GVX-5H black 9915 has an optimized flowability and is suitable for injection molding technical parts, exhibiting exceptional characteristics even after moisture absorption:
- high stiffness and strength
- high dimensional stability, very low warpage
- good chemical resistance
- very good surface finish
Information provided by EMS Grivory
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.56 g/cc | 0.0564 lb/in3 | ISO 1183 |
| 吸水率 | 4.0 % | 4.0 % | ISO 62 |
| 水分吸收 | 1.40 % | 1.40 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 |
| 线性成型收缩率，横向 | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 球压硬度 | 265 MPa | 38400 psi | conditioned; ISO 2039-1 |
| 290 MPa | 42100 psi | dry; ISO 2039-1 | |
| 抗张强度(断裂) | 220 MPa | 31900 psi | conditioned; ISO 527-1/-2 |
| 250 MPa | 36300 psi | dry; ISO 527-1/-2 | |
| 伸长率 (断裂) | 2.5 % | 2.5 % | dry; ISO 527-1/-2 |
| 2.5 % | 2.5 % | conditioned; ISO 527-1/-2 | |
| 拉伸模量 | 17.0 GPa | 2470 ksi | conditioned; ISO 527-1/-2 |
| 18.0 GPa | 2610 ksi | dry; ISO 527-1/-2 | |
| 简支梁无缺口冲击强度 | 7.50 J/cm2 | 35.7 ft-lb/in2 | conditioned; ISO 179/1eU |
| 8.00 J/cm2 | 38.1 ft-lb/in2 | dry; ISO 179/1eU | |
| 6.00 J/cm2
@Temperature 30.0 °C
|
28.6 ft-lb/in2
@Temperature 86.0 °F
|
conditioned; ISO 179/1eU | |
| 6.50 J/cm2
@Temperature 30.0 °C
|
30.9 ft-lb/in2
@Temperature 86.0 °F
|
dry; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 1.50 J/cm2 | 7.14 ft-lb/in2 | dry; ISO 179/1eA |
| 1.50 J/cm2 | 7.14 ft-lb/in2 | conditioned; ISO 179/1eA | |
| 1.50 J/cm2
@Temperature 30.0 °C
|
7.14 ft-lb/in2
@Temperature 86.0 °F
|
dry; ISO 179/1eU | |
| 1.50 J/cm2
@Temperature 30.0 °C
|
7.14 ft-lb/in2
@Temperature 86.0 °F
|
conditioned; ISO 179/1eU |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | dry; IEC 60093 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 | |
| 表面电阻 | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| 介电强度 | 33.0 kV/mm | 838 kV/in | dry; IEC 60243-1 |
| 33.0 kV/mm | 838 kV/in | conditioned; IEC 60243-1 | |
| 相比耐漏电起痕指数(CTI) | 600 V | 600 V | conditioned; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 20.0 μm/m-°C | 11.1 μin/in-°F | ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | 50.0 μm/m-°C | 27.8 μin/in-°F | ISO 11359-1/-2 |
| 熔融温度 | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| 最高工作温度, Air | 100 - 120 °C | 212 - 248 °F | long term; EMS |
| 220 °C | 428 °F | short term; EMS | |
| 载荷下热变形温度(1.8 MPa) | 245 °C | 473 °F | ISO 75-1/-2 |
| 载荷下热变形温度(8.0 MPa) | 175 °C | 347 °F | ISO 75-1/-2 |
| 可燃性(UL94) | HB | HB | IEC 60695-11-10 |
| 材料描述 | 测试方法 | |
|---|---|---|
| 汽车 | Air intake sytems | |
| Automotive electr. and electronics, lighting | ||
| Cooling and climate control | ||
| Exterior | ||
| Interior | ||
| Powertrain and Chassis | ||
| 电器及电子产品 | Connectors | |
| Electrical appliances | ||
| Electrical equipment | ||
| Energy distribution | ||
| Mobile phones and other portable devices | ||
| 形式 | Granules | |
| 工业和消费品 | Housewares | |
| Hydraulics Pneumatics | ||
| Mechanical Engineering | ||
| Power transmission | ||
| Sanitary, water and gas supply | ||
| Sports Leisure | ||
| Tools Accessories | ||
| 加工 | Injection Molding | |
| 产品属性 | Improved flowability and demoulding | |
| Partially aromatic Polyamide |
产品描述：
Grivory GVX-5H black 9915是一种50%的玻璃纤维增强工程热塑性材料，基于半结晶聚酰胺与部分芳香族共聚酰胺的组合。Grivory GVX-5H black 9915具有优化的流动性，适用于注塑技术零件，即使在吸湿后也表现出优异的特性：
高刚度和强度
高尺寸稳定性，极低翘曲
良好的耐化学性
非常好的表面光洁度
Grivory GVX-5H black 9915是压铸合金的经济替代品。