苯乙烯-丁二烯-苯乙烯嵌段共聚物
AKelastomers
产品说明:
Injection- and blow-molding grade. For transparent products with superior impact strength. Blended with GPPS (general-purpose polystyrene) or SC for films with good thermal stability. Capability for profile-extrusion products. It is supplied in pellet form.
Cosmetics caps, stationery goods, other consumer goods. Blended with GPPS for PSP* laminate films and IC magazine rails, and with SC* for shrink films.
* Styrenic copolymer from PS Japan Corp. similar to Asaflex? 825 in refraction index, resulting in blends that provide sheet transparency significantly higher than attainable with any GPPS.
Asaflex? 825 物性表
基本信息 |
|
特性 |
|
用途 |
Cosmetic Packaging
Water Sports Equipment
薄膜
层压板
文具
消费品应用领域
型材
|
外观 |
|
形式 |
|
加工方法 |
|
物理性能 |
额定值 |
单位制 |
测试方法 |
密度 |
1.02 |
g/cm3 |
ISO 1183 |
熔流率(熔体流动速率)(200°C/5.0 kg) |
6.0 |
g/10 min |
ISO 1133 |
收缩率 |
0.20 到 0.80 |
% |
|
吸水率(23°C, 24 hr) |
0.10 |
% |
ISO 62 |
硬度 |
额定值 |
单位制 |
测试方法 |
洛氏硬度(R 计秤) |
55 |
|
ISO 2039-2 |
肖氏硬度(邵氏 D) |
71 |
|
ISO 868 |
机械性能 |
额定值 |
单位制 |
测试方法 |
拉伸应力(屈服) |
27.0 |
MPa |
ISO 527-2/5 |
拉伸应变(断裂) |
200 |
% |
ISO 527-2/5 |
弯曲模量 |
1200 |
MPa |
ISO 178 |
弯曲应力 |
37.0 |
MPa |
ISO 178 |
冲击性能 |
额定值 |
单位制 |
测试方法 |
简支梁缺口冲击强度(完全断裂) |
2.0 |
kJ/m2 |
ISO 179 |
简支梁无缺口冲击强度(完全断裂) |
100 |
kJ/m2 |
ISO 179 |
热性能 |
额定值 |
单位制 |
测试方法 |
热变形温度(1.8 MPa, 未退火) |
57.0 |
°C |
ISO 75-2/A |
维卡软化温度 |
82.0 |
°C |
ISO 306/A50 |
光学性能 |
额定值 |
单位制 |
测试方法 |
透射率(2000 μm) |
90.0 |
% |
ISO 3537 |
雾度(2000 μm) |
0.50 |
% |
ISO 3537 |