Plexiglas V920

Polymethyl Methacrylate Acrylic

Altuglas International of Arkema Inc.

产品说明：

Plexiglas V920 is a General-purpose thermoplastic acrylic resin formulated for injection molding and extrusion applications. It is characterized by its very high melt flow. Plexiglas V920 has excellent weatherability and optical properties allowing it to excel in applications requiring outdoor stability, high quality surface appearance and/or precision optics. Plexiglas V920 is easy to process due to its exceptional thermal stability, extrusion melt strength, and excellent tool surface reproduction and release properties. Supplemental moldflow simulation data is available. It has excellent resistance to many chemicals including solutions of inorganic acids, alkalis and aliphatic hydrocarbons such as VMP naphtha and heptane. Additionally, it is virtually unaffected by a wide range of commercial products including many beverages, foodstuffs, detergent solutions and cleaners.

物性信息：

基本信息
黄卡编号	E39437-231440 E39437-231441
特性	尺寸稳定性良好 抗划伤性高 抗紫外线性能良好 良好的颜色稳定性 耐气候影响性能良好 清晰度，高 热稳定性，良好 收缩性低 无 BPA
用途	光学应用 汽车领域的应用 消费品应用领域
机构评级	FDA 21 CFR 177.1010
RoHS 合规性	RoHS 合规
外观	半透明 不透明 可用颜色 清晰/透明
形式	粒子
加工方法	挤出 注射成型

物理性能	额定值	单位制	测试方法
比重	1.18	g/cm3	ASTM D792
熔流率（熔体流动速率）(230°C/3.8 kg)	8.0	g/10 min	ASTM D1238
收缩率 - 流动	0.20 到 0.60	%	ASTM D955
吸水率(24 hr)	0.30	%	ASTM D570

硬度	额定值	单位制	测试方法
洛氏硬度(M 级)	90		ASTM D785

机械性能	额定值	单位制	测试方法
拉伸模量	3100	MPa	ASTM D638
抗张强度(屈服)	68.9	MPa	ASTM D638
伸长率(断裂)	5.0	%	ASTM D638
弯曲模量	3100	MPa	ASTM D790
弯曲强度(屈服)	103	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度(23°C)	16	J/m	ASTM D256

热性能	额定值	单位制	测试方法
载荷下热变形温度1			ASTM D648
0.45 MPa, 退火	92.8	°C	ASTM D648
1.8 MPa, 退火	90.6	°C	ASTM D648
维卡软化温度
--	100	°C	ASTM D15252
--	91.1	°C	ASTM D15253
导热系数	0.19	W/m/K	ASTM C177

可燃性	额定值		测试方法
UL 阻燃等级	HB		UL 94

光学性能	额定值	单位制	测试方法
折射率4	1.490		ASTM D542
透射率(3180 μm)	92.0	%	ASTM D1003
雾度(3180 μm)	1.0	%	ASTM D1003

补充信息	额定值		测试方法
ASTM Classification	PMMA 0121V4		ASTM D788

注射	额定值	单位制
干燥温度	79.4 到 87.8	°C
干燥时间	4.0	hr
建议的最大水分含量	0.10	%
建议注射量	50	%
建议的最大回制料比例	20	%
料筒后部温度	204	°C
料筒中部温度	210	°C
料筒前部温度	216	°C
射嘴温度	210	°C
加工（熔体）温度	271	°C
模具温度	65.6 到 85.0	°C
注射速度	快速
背压	0.689	MPa
螺杆转速	50 到 100	rpm
螺杆长径比	15.0:1.0到20.0:1.0
螺杆压缩比	2.0:1.0 至 2.5:1.0
排气孔深度	0.051	mm

备注
1 .	Annealing cycle: 4hrs @ 176°F
2 .	速率 A (50°C/h), 压 力1 (10N)
3 .	速率 A (50°C/h), 载荷2 (50N)
4 .	ND @ 72°F