Plexalloy NTA-1 (PMMA)
Plexalloy NTA-3 (PMMA)
Plexiglas 6N (PMMA)
Plexiglas 7H (PMMA)
Plexiglas 7M (PMMA)
Plexiglas 7N (PMMA)
Plexiglas 8H (PMMA)
Plexiglas 8N (PMMA)
Plexiglas CR30 (PMMA)
Plexiglas CR50 (PMMA)
Plexiglas df20 8N (PMMA)
Plexiglas df21 8N (PMMA)
Plexiglas df22 7H (PMMA)
Plexiglas df22 8N (PMMA)
Plexiglas df22 zk6BR (PMMA)
Plexiglas df23 7H (PMMA)
Plexiglas df23 8N (PMMA)
Plexiglas df23 zk6BR (PMMA)
Plexiglas DR M2 (PMMA)
Plexiglas DR UVA20 (PMMA)
Plexiglas DR (PMMA)
Plexiglas Frosted DR (PMMA)
Plexiglas Frosted V045 (PMMA)
Plexiglas FT15 (PMMA)
Plexiglas G (PMMA)
Plexiglas Heatstop 8N (PMMA)
Plexiglas HFI10 (PMMA)
Plexiglas HFI7 (PMMA)
Plexiglas HT121 (PMMA)
Plexiglas hw55 (PMMA)
Plexiglas MC (PMMA)
Plexiglas MI7 (PMMA)
Plexiglas POQ62 (PMMA)
Plexiglas POQ64 (PMMA)
Plexiglas POQ66 (PMMA)
Plexiglas SG10 (PMMA)
Plexiglas V044 (PMMA)
Plexiglas V045 (PMMA)
Plexiglas V045i (PMMA)
Plexiglas V052 (PMMA)
Plexiglas V052i (PMMA)
Plexiglas V825 (PMMA)
Plexiglas V825-HID (PMMA)
Plexiglas V825-UVA5A (PMMA)
Plexiglas V826 (PMMA)
Plexiglas V920 (PMMA)
Plexiglas VH (PMMA)
Plexiglas VM (PMMA)
Plexiglas VS (PMMA)
Plexiglas VS-UVT (PMMA)
Plexiglas zk20 (PMMA)
Plexiglas zk30 (PMMA)
Plexiglas zk40 (PMMA)
Plexiglas zk4BR (PMMA)
Plexiglas zk4HC (PMMA)
Plexiglas zk50 (PMMA)
Plexiglas zk5BR (PMMA)
Plexiglas zk5HC (PMMA)
Plexiglas zk5HF (PMMA)
Plexiglas zk6BR (PMMA)
Plexiglas zk6HC (PMMA)
Plexiglas zk6HF (PMMA)
Plexiglas HFI10
基本信息 | |
---|---|
黄卡编号 | |
添加剂 |
|
特性 |
|
用途 |
|
机构评级 |
|
RoHS 合规性 |
|
外观 |
|
形式 |
|
加工方法 |
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
比重 | 1.15 | g/cm3 | ASTM D792 |
熔流率(熔体流动速率)(230°C/3.8 kg) | 3.3 | g/10 min | ASTM D1238 |
收缩率 - 流动 | 0.30 到 0.80 | % | ASTM D955 |
吸水率(24 hr) | 0.40 | % | ASTM D570 |
硬度 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
洛氏硬度(M 级) | 38 | ASTM D785 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | 1860 | MPa | ASTM D638 |
抗张强度(断裂) | 37.9 | MPa | ASTM D638 |
伸长率(断裂) | 50 | % | ASTM D638 |
弯曲模量 | 1860 | MPa | ASTM D790 |
弯曲强度(屈服) | 71.0 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
悬壁梁缺口冲击强度(23°C) | 48 | J/m | ASTM D256 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
载荷下热变形温度1 | ASTM D648 | ||
0.45 MPa, 退火 | 88.9 | °C | ASTM D648 |
1.8 MPa, 退火 | 79.4 | °C | ASTM D648 |
维卡软化温度 | |||
-- | 93.9 | °C | ASTM D15252 |
-- | 82.8 | °C | ASTM D15253 |
导热系数 | 0.22 | W/m/K | ASTM C177 |
可燃性 | 额定值 | 测试方法 | |
---|---|---|---|
UL 阻燃等级 | HB | UL 94 |
光学性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
折射率4 | 1.490 | ASTM D542 | |
透射率(3180 μm) | 90.0 | % | ASTM D1003 |
雾度(3180 μm) | 1.0 | % | ASTM D1003 |
补充信息 | 额定值 | 测试方法 | |
---|---|---|---|
ASTM Classification | PMMA 0231V2 | ASTM D788 |
注射 | 额定值 | 单位制 | |
---|---|---|---|
干燥温度 | 82.2 到 87.8 | °C | |
干燥时间 | 4.0 | hr | |
建议的最大水分含量 | 0.10 | % | |
建议注射量 | 50 | % | |
建议的最大回制料比例 | 20 | % | |
料筒后部温度 | 221 | °C | |
料筒中部温度 | 227 | °C | |
料筒前部温度 | 232 | °C | |
射嘴温度 | 227 | °C | |
加工(熔体)温度 | 271 | °C | |
模具温度 | 37.8 到 87.8 | °C | |
注射速度 | 中等 | ||
背压 | 0.689 | MPa | |
螺杆转速 | 50 到 100 | rpm | |
螺杆长径比 | 15.0:1.0到20.0:1.0 | ||
螺杆压缩比 | 2.0:1.0 至 2.5:1.0 | ||
排气孔深度 | 0.051 | mm |
备注 | |
---|---|
1 . | Annealing cycle: 4hrs @ 176°F |
2 . | 速率 A (50°C/h), 压 力1 (10N) |
3 . | 速率 A (50°C/h), 载荷2 (50N) |
4 . | ND @ 72°F |
批发说明本公司支持提倡各种优惠活动,多买多优惠,薄利多销为原则,赢得广大的口碑 ★ 客户拿一包试模打样,按批发价供给,祝客户试摸成功 ★ 客户试摸成功,订购低于1吨按低于当天市场价格优惠供给 ★ 客户订货1吨以上免费可送货上门;,按批发价格供给,长期合作。 ★ 东莞山鑫塑胶,欢迎你选购! 运费说明:支持物流,快递和货运; 支持现金,银行转账. ★ 本公司原料低于1吨,不承担运费,订货1吨以上广东地区可送货上门; 省外客户物流,快递或货运; 不便之处敬请谅解,谢谢! ★ 选用物流或者快递的买家,请先确认当地是否有该物流或快递的营业网点。 ★ 原料到厂后,请不要拆外包装,应先仔细检查原料的外包装是否完好及原料型号是否与您所订购原料型号相匹配。 ★ 货物送达后,请*时间检查,发现物流过程中出现大量包装损坏及原料外漏的,请让物流人员出具证明并保存,并在24小时内与我们联系。 ★ 如发货后未能及时收到,请及时与我们联系。 ★ 本公司原料售后的注塑加工由客户负责,如需帮助,我公司工程部将竭尽所能与您共同协商处理。 ★ 本公司随货的基本资料包括《送货单》两联、《货款收据》一张、《商务经理名片》一张 注:25公斤/包起订,批量可折扣,款到发货或物流代收款. 珠三角一天内到达,国内各地五天内到货. 温馨提示:因塑料行情每天都会有变更,页面上有些报价可能会与当天实际报价有所差异,仅供参考! 若需要材料详细物性资料及环保证书等,请电邮:tzplas@163.com索取。感谢您的配合与支持! 1吨以上在广东省以内可以免费送货上门 ...详细请咨询 18926874899罗生 |