Kingfa FRHIPS-100 Kingfa PS (HIPS)
Kingfa FRHIPS-113 Kingfa PS (HIPS)
Kingfa FRHIPS-1162 Kingfa PS (HIPS)
Kingfa FRHIPS-117 Kingfa PS (HIPS)
Kingfa FRHIPS-220 Kingfa PS (HIPS)
Kingfa FRHIPS-301 Kingfa PS (HIPS)
Kingfa FRHIPS-702 Kingfa PS (HIPS)
Kingfa FRHIPS-722 Kingfa PS (HIPS)
Kingfa FRHIPS-8002 Kingfa PS (HIPS)
Kingfa FRHIPS-8002U Kingfa PS (HIPS)
Kingfa FRHIPS-930 Kingfa PS (HIPS)
Kingfa FRHIPS-960 Kingfa PS (HIPS)
Kingfa FRHIPS-960PC Kingfa PS (HIPS)
Kingfa FRHIPS-980 Kingfa PS (HIPS)
Kingfa FRHIPSV-0 Kingfa PS (HIPS)
Kingfa HIPS-5197 Kingfa PS (HIPS)
Kingfa FRHIPS-960 Flame Retardant Polystyrene
Polystyrene, Flame Retardant
Kingfa Sci. amp; Tech. Co.
产品说明：
- Features:
- UL 94 V-0 @ 1.6mm, V-0 @ 3.2mm
- Excellent balance properties, Non-DPO
- Good heat stability
- Color tailor-made for client
- Applications:
- Injection molding
- Gas assistant molding
- Printer and photocopier cabinet
- Electric and electronic cabinet
Information Provided by Kingfa Sci. Tech. Co., Ltd.
物性信息：
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.15 g/cc
@Temperature 23.0 °C
|
1.15 g/cc
@Temperature 73.4 °F
|
ASTM D792 |
| 线性成型收缩率 | 0.0040 - 0.0060 cm/cm
@Temperature 23.0 °C
|
0.0040 - 0.0060 in/in
@Temperature 73.4 °F
|
ASTM D955 |
| 熔体流动速率 | 10 g/10 min
@Load 5.00 kg, Temperature 200 °C
|
10 g/10 min
@Load 11.0 lb, Temperature 392 °F
|
ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 24.0 MPa | 3480 psi | 50mm/min; ASTM D638 |
| 伸长率 (断裂) | 45 % | 45 % | 50mm/min; ASTM D638 |
| 弯曲强度 | 40.0 MPa | 5800 psi | 2mm/min; ASTM D790 |
| 弯曲模量 | 2.25 GPa | 326 ksi | 2mm/min; ASTM D790 |
| 悬壁梁缺口冲击强度 | 1.04 J/cm
@Thickness 3.20 mm, Temperature 23.0 °C
|
1.95 ft-lb/in
@Thickness 0.126 in, Temperature 73.4 °F
|
ASTM D256 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Hot Ball Pressure Test | 85.0 °C
@Thickness 2.00 mm
|
185 °F
@Thickness 0.0787 in
|
IEC695-10-2 |
| 载荷下热变形温度(1.8 MPa) | 75.0 °C
@Thickness 6.40 mm
|
167 °F
@Thickness 0.252 in
|
ASTM D648 |
| 可燃性(UL94) | V-0
@Thickness 1.60 mm
|
V-0
@Thickness 0.0630 in
|
|
| V-0
@Thickness 3.20 mm
|
V-0
@Thickness 0.126 in
|
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工温度 | = 250 °C | = 482 °F | |
| 料筒后部温度 | 182 - 205 °C | 360 - 401 °F | Start Point: 190°C |
| 料筒中部温度 | 205 - 230 °C | 401 - 446 °F | Start Point: 215°C |
| 料筒前部温度 | 215 - 240 °C | 419 - 464 °F | Start Point: 225°C |
| 加工（熔体）温度 | 220 - 245 °C | 428 - 473 °F | Start Point: 230°C |
| 模具温度 | 30.0 - 60.0 °C | 86.0 - 140 °F | Start Point: 50°C |
| 干燥温度 | 70.0 °C
@Time 7200 sec
|
158 °F
@Time 2.00 hour
|
Pre-dry |
| 背压 | 5.00 - 15.0 MPa | 725 - 2180 psi |
| 材料描述 | 测试方法 | |
|---|---|---|
| 射速 | Slow to Moderate |