TOTAL 2002 SN 58 HDPE
TOTAL 2003 SN 53 HDPE
TOTAL 2008 SN 60 HDPE
TOTAL 2285 HDPE
TOTAL 2287 HDPE
TOTAL 3344N HDPE
TOTAL 3407B HDPE
TOTAL 4206 B HDPE
TOTAL 46060 UV HDPE
TOTAL 49080 UV HDPE
TOTAL 50100.1 HDPE
TOTAL 50100.2 (sheet) HDPE
TOTAL 50100.2 HDPE
TOTAL 51090 HDPE
TOTAL 5202 LD HDPE
TOTAL 5202 HDPE
TOTAL 53090 HDPE
TOTAL 54050 HDPE
TOTAL 5502 (EU) HDPE
TOTAL 5502 (US) HDPE
TOTAL 5502 BZ HDPE
TOTAL 5502 R3 HDPE
TOTAL 5503 HDPE
TOTAL 55090 HDPE
TOTAL 55200 HDPE
TOTAL 56020 S UHMWPE
TOTAL 5802 HDPE
TOTAL 6410 HDPE
TOTAL 6420 HDPE
TOTAL 7194 HDPE
TOTAL 7195 HDPE
TOTAL 7208 HDPE
TOTAL 8183 HDPE
TOTAL 9458 HDPE
TOTAL B5845 HDPE
TOTAL BM 593 HDPE
TOTAL BM 961 HDPE
TOTAL BM 962 HDPE
TOTAL CD 4300 HDPE
TOTAL CD-471 HDPE
TOTAL ESD 201 B HDPE
TOTAL HD 5809 S01 HDPE
TOTAL HD 6081 HDPE
TOTAL HD 6221 HDPE
TOTAL HD55110 S02 HDPE
TOTAL 55060 HDPE
TOTAL 6280 HDPE
TOTAL XRC 20 B HDPE
TOTAL HL 428 HDPE
TOTAL HL 535 HDPE
TOTAL HL 717 HDPE
TOTAL HP 401 N HDPE
TOTAL mPE M 5021 HDPE
TOTAL mPE M 6091 HDPE
TOTAL MS 201 B HDPE
TOTAL MS 201 BN HDPE
TOTAL MS201 BN-NA HDPE
TOTAL SB 1461 HDPE
TOTAL SI 508 HDPE
TOTAL XLS 12 B HDPE
TOTAL XS10 B HDPE
TOTAL XS10 BRS HDPE
TOTAL XS10 H HDPE
TOTAL XS10 HDPE
TOTAL XS10 OS HDPE
TOTAL XS10 YS HDPE
TOTAL XT10 N HDPE
Total HDPE 46060 UV High Density Polyethylene - Large Part Blow Molding ResinHigh Density Polyethylene (HDPE), Blow Molding Grade
Total Atofina
产品说明:
Polyethylene:High molecular weight, high density large part blow molding resin.
Characteristics:
- Good melt strength
- Good impact and creep resistance
- Excellent stress cracking resistance
- Excellent stacking strength
- Good rigidity
- ASTM D 1248 - Type III, Class A, Category 5
- ASTM D 4976-89-PE235
- FDA Compliant
Applications:
- Shipping containers
- Industrial chemical tanks
- Intermediate bulk containers
- Agricultural chemical tanks
Information provided by Total Petrochemicals.
物性信息:
物理性能
额定值 (公制)
额定值 (英制)
测试方法
比重
0.946 g/cc
0.946 g/cc
ASTM D792
ESCR 100% Igepal?
= 1000 hour
= 1000 hour
F50; ASTM D1693
ESCR 10% Igepal?
= 1000 hour
= 1000 hour
F50; ASTM D1693
熔体流动速率
6.0 g/10 min
@Load 21.6 kg, Temperature 190 °C
6.0 g/10 min
@Load 47.6 lb, Temperature 374 °F
ASTM D1238
机械性能
额定值 (公制)
额定值 (英制)
测试方法
抗张强度(断裂)
36.8 MPa
5340 psi
ASTM D638
抗张强度(屈服)
24.7 MPa
3580 psi
ASTM D638
伸长率 (断裂)
630 %
630 %
ASTM D638
弯曲模量
0.8115 GPa
@Strain 0.400 %
117.7 ksi
@Strain 0.400 %
ASTM D790
悬壁梁缺口冲击强度
5.61 J/cm
@Thickness 3.17 mm
10.5 ft-lb/in
@Thickness 0.125 in
ASTM D256
热性能
额定值 (公制)
额定值 (英制)
测试方法
维卡软化温度
124 °C
255 °F
ASTM D3417
加工性能
额定值 (公制)
额定值 (英制)
测试方法
加工温度
188 - 227 °C
370 - 440 °F
Blow Molding Stock Temp.
Characteristics:
- Good melt strength
- Good impact and creep resistance
- Excellent stress cracking resistance
- Excellent stacking strength
- Good rigidity
- ASTM D 1248 - Type III, Class A, Category 5
- ASTM D 4976-89-PE235
- FDA Compliant
Applications:
- Shipping containers
- Industrial chemical tanks
- Intermediate bulk containers
- Agricultural chemical tanks
Information provided by Total Petrochemicals.
物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
比重 | 0.946 g/cc | 0.946 g/cc | ASTM D792 |
ESCR 100% Igepal? | = 1000 hour | = 1000 hour | F50; ASTM D1693 |
ESCR 10% Igepal? | = 1000 hour | = 1000 hour | F50; ASTM D1693 |
熔体流动速率 | 6.0 g/10 min
@Load 21.6 kg, Temperature 190 °C
|
6.0 g/10 min
@Load 47.6 lb, Temperature 374 °F
|
ASTM D1238 |
机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
抗张强度(断裂) | 36.8 MPa | 5340 psi | ASTM D638 |
抗张强度(屈服) | 24.7 MPa | 3580 psi | ASTM D638 |
伸长率 (断裂) | 630 % | 630 % | ASTM D638 |
弯曲模量 | 0.8115 GPa
@Strain 0.400 %
|
117.7 ksi
@Strain 0.400 %
|
ASTM D790 |
悬壁梁缺口冲击强度 | 5.61 J/cm
@Thickness 3.17 mm
|
10.5 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
维卡软化温度 | 124 °C | 255 °F | ASTM D3417 |
加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
---|---|---|---|
加工温度 | 188 - 227 °C | 370 - 440 °F | Blow Molding Stock Temp. |