SEETEC CF050 HDPE
SEETEC CJ560 HDPE
SEETEC CJ563 HDPE
SEETEC CJ680 HDPE
SEETEC CJ681 HDPE
SEETEC CJ770 HDPE
SEETEC CJ870 HDPE
SEETEC CJ970 HDPE
SEETEC PB150 HDPE
SEETEC PB150 LG HDPE
SEETEC PB160 HDPE
SEETEC PB172 HDPE
SEETEC PB270 HDPE
SEETEC PB270 LG HDPE
SEETEC PB272 HDPE
SEETEC PB279 HDPE
SEETEC PB283 HDPE
SEETEC PB283 LG HDPE
SEETEC PB382 HDPE
SEETEC PF150 HDPE
SEETEC PF150 LG HDPE
SEETEC PH140 HDPE
SEETEC PH143 HDPE
SEETEC PH150 LG HDPE
SEETEC PH150 HDPE
SEETEC PH153 HDPE
SEETEC PH159 HDPE
SEETEC PH160 HDPE
SEETEC PH162 HDPE
SEETEC PH162 LG HDPE
SEETEC PH270 HDPE
SEETEC PJ489 HDPE
SEETEC PM360 HDPE
SEETEC PM360 LG HDPE
SEETEC SJ680 HDPE
SEETEC HDPE PB150
High Density Polyethylene
LG Chem Ltd.
产品说明：
Application
Fuel Tank, IBC, Jerry can, Agri-chemical container
Feature
This high molecular weight, hexene copolymer is tailored for high impact blow-molded containers that require:
Process : Phillips slurry process
This resin meet FDA21 CFR 177.1520
Additives : Anti-Oxidants
Fuel Tank, IBC, Jerry can, Agri-chemical container
Feature
This high molecular weight, hexene copolymer is tailored for high impact blow-molded containers that require:
- Excellent processability
- High impact strength at low temperature
- Outstanding stress crack resistance(ESCR)
- Good melt strength
Process : Phillips slurry process
This resin meet FDA21 CFR 177.1520
Additives : Anti-Oxidants
物性信息：
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.946 | g/cm3 | ASTM D1505 |
| 熔流率（熔体流动速率）(190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| 抗环境应力开裂(F50) | 500 | hr | ASTM D1693 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 | 60 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 23.0 | MPa | ASTM D638 |
| 伸长率(断裂) | 600 | % | ASTM D638 |
| 弯曲模量 | 830 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 无缺口悬臂梁冲击(23°C) | 无断裂 | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 125 | °C | ASTM D1525 |
| 熔融峰值温度1 | 130 | °C | ASTM D3418 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 加工（熔体）温度 | 180 | °C |
| 备注 | |
|---|---|
| 1 . | Condition: 10°C/min |