东莞市常平浩云塑胶经营部
Samsung Total B220A HDPE
Samsung Total B221B HDPE
Samsung Total B230A HDPE
Samsung Total C430A HDPE
Samsung Total F120A HDPE
Samsung Total F120U HDPE
Samsung Total P110A HDPE
Samsung Total P110BL HDPE
Samsung Total P110P HDPE
Samsung Total P110PT12 HDPE
Samsung Total P110Y HDPE
Samsung Total P11CB HDPE
Samsung Total P200BL HDPE
Samsung Total P200CB HDPE
Samsung Total P200Y50 HDPE
Samsung Total R901P HDPE
Samsung Total R902P HDPE
Samsung Total R902S HDPE
Samsung Total R902U HDPE
Samsung Total R903U HDPE
Samsung Total R904U HDPE
Samsung Total R906P HDPE
Samsung Total R906U HDPE
Samsung Total R908P HDPE
Samsung Total R908U HDPE
Samsung Total Y910A HDPE
Hanwha Total PE F120A
High Density Polyethylene
HANWHA TOTAL PETROCHEMICALS Co., Ltd.
产品说明：
F120A is a high-density polyethylene resin for films. This grade is designed to be processed in conventional blown film equipment. F120A is suited to general-purpose packaging films and shopping bag applications.
物性信息：
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.956 | g/cm3 | ASTM D1505 |
| 熔流率（熔体流动速率）(190°C/2.16 kg) | 0.044 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度(R 级) | 55 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 屈服 | 22.6 | MPa | ASTM D638 |
| 断裂 | 29.4 | MPa | ASTM D638 |
| 明显的弯曲模量 | 981 | MPa | ASTM D747 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 20 | μm | |
| 抗张强度 | ASTM D882 | ||
| MD : 断裂, 20 μm | 53.9 | MPa | ASTM D882 |
| TD : 断裂, 20 μm | 49.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 20 μm | 380 | % | ASTM D882 |
| TD : 断裂, 20 μm | 450 | % | ASTM D882 |
| 落锤冲击(20 μm) | 200 | g | ASTM D1709 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | 290 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 脆化温度 | -80.0 | °C | ASTM D746 |
| 维卡软化温度 | 124 | °C | ASTM D15251 |
| 补充信息 |
|---|
| Elmendorf Tear Strength MD, ASTM D785: 6 kg force/cm2Elmendorf Tear Strength TD, ASTM D785: 200 kg force/cm2 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 料筒1区温度 | 160 到 190 | °C | |
| 料筒2区温度 | 160 到 190 | °C | |
| 料筒3区温度 | 160 到 190 | °C | |
| 料筒4区温度 | 160 到 190 | °C | |
| 料筒5区温度 | 160 到 190 | °C | |
| 口模温度 | 180 到 210 | °C |
| 挤压说明 |
|---|
| Blow up ratio: 3 to 6Frost Line Height: 40 to 120 cm |
| 备注 | |
|---|---|
| 1 . | 压 力1 (10N) |