SABIC HDPE PCG40053

High Density Polyethylene

SABIC Americas, Inc.

产品说明：

SABIC HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity.

SABIC HDPE PCG40053 is designed for the injection moulding of healthcare packaging, caps and closures and other parts for medical packaging. This grade has a very high impact resistance, even at low temperatures.

SABIC HDPE PCG40053 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.

物性信息：

基本信息
特性	纯度高 抗撞击性，高 耐低温冲击
用途	包装 护罩 外壳 医疗/护理用品 医用包装
机构评级	EP Unspecified Rating USP 第VI类
形式	粒子
加工方法	注射成型

物理性能	额定值	单位制	测试方法
密度	0.953	g/cm3	ISO 1183
熔流率（熔体流动速率）			ISO 1133
190°C/2.16 kg	4.7	g/10 min	ISO 1133
190°C/5.0 kg	13	g/10 min	ISO 1133
溶化体积流率（MVR）			ISO 1133
190°C/2.16 kg	5.80	cm3/10min	ISO 1133
190°C/5.0 kg	17.0	cm3/10min	ISO 1133
抗环境应力开裂1(60°C, 3.00 mm, Rhodacal-DS10)	95.0	hr	内部方法

硬度	额定值	单位制	测试方法
肖氏硬度(邵氏 D, 模压成型)	61		ISO 868

机械性能	额定值	单位制	测试方法
拉伸模量(2.00 mm, 模压成型)	1100	MPa	ISO 527-2/1BA/50
拉伸应力			ISO 527-2/1BA/50
屈服, 2.00 mm, 模压成型	26.0	MPa	ISO 527-2/1BA/50
断裂, 2.00 mm, 模压成型	25.0	MPa	ISO 527-2/1BA/50
拉伸应变(断裂, 2.00 mm, 模压成型)	200	%	ISO 527-2/1BA/50
拉伸蠕变模量			ISO 899-1
1 hr	500	MPa	ISO 899-1
1000 hr	225	MPa	ISO 899-1

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度			ISO 180/A
-30°C, 模压成型	4.0	kJ/m2	ISO 180/A
23°C, 模压成型	4.0	kJ/m2	ISO 180/A

热性能	额定值	单位制	测试方法
热变形温度(0.45 MPa, 未退火)	81.0	°C	ISO 75-2/B
维卡软化温度	124	°C	ISO 306/A
溶融温度（DSC）	132	°C	DIN 53765
Enthalpy Change	203	J/g	DIN 53765

备注
1 .	2 MPa