东莞市常平浩云塑胶经营部
SABIC 0863F HDPE
SABIC B4406 HDPE
SABIC B4520 HDPE
SABIC B4660 HDPE
SABIC B4660AB HDPE
SABIC B5202 HDPE
SABIC B5205 HDPE
SABIC B5209 HDPE
SABIC B5210 HDPE
SABIC B5309 HDPE
SABIC B5411 HDPE
SABIC B5421 HDPE
SABIC B5429 HDPE
SABIC B5823 HDPE
SABIC B5933 HDPE
SABIC B6246 HDPE
SABIC B6246LS HDPE
SABIC F00950 HDPE
SABIC F00952 HDPE
SABIC F00952EQ HDPE
SABIC F00952J HDPE
SABIC F01552 HDPE
SABIC F04660 HDPE
SABIC F4520 HDPE
SABIC FI0644 HDPE
SABIC FI1157 HDPE
SABIC ICP4907S HDPE
SABIC ICP5505 HDPE
SABIC ICP5602 HDPE
SABIC M100053 HDPE
SABIC M100053C HDPE
SABIC M100053CO HDPE
SABIC M200056 HDPE
SABIC M300054 HDPE
SABIC M30053S HDPE
SABIC M40053 HDPE
SABIC M40053CO HDPE
SABIC M40053S HDPE
SABIC M40053SE HDPE
SABIC M40060S HDPE
SABIC M80063 HDPE
SABIC M80063S HDPE
SABIC M80064 HDPE
SABIC M80064E HDPE
SABIC M80064S HDPE
SABIC M80064SE HDPE
SABIC PCG40053 HDPE
SABIC PCG5421 HDPE
SABIC PCG80063 HDPE
SABIC Vestolen A 4062R 10000 HDPE
SABIC Vestolen A 4062R 62429 HDPE
SABIC Vestolen A 4062R 62437 HDPE
SABIC Vestolen A 4062R 65308 HDPE
SABIC Vestolen A 4062R HDPE
SABIC Vestolen A 5017 HDPE
SABIC Vestolen A 5061R 10000 HDPE
SABIC Vestolen A 5061R 62437 HDPE
SABIC Vestolen A 5061R 63363 HDPE
SABIC Vestolen A 5061R 65308 HDPE
SABIC Vestolen A 6012 HDPE
SABIC Vestolen A 6013 HDPE
SABIC Vestolen A 6060R 10000 HDPE
SABIC Vestolen A 6060R 62434 HDPE
SABIC Vestolen A 6060R 63363 HDPE
SABIC Vestolen A 6060R 65307 HDPE
SABIC Vestolen A 6060R HDPE
SABIC HDPE F00952
High Density Polyethylene Copolymer
Saudi Basic Industries Corporation (SABIC)
产品说明：
SABIC HDPE F00952 resin is a high molecular weight high density polyethylene copolymer which has been designed specifically for blown film extrusion. Its high molecular weight, broad molecular distribution and high density combine succesfully to give excellent extrudability with high film strength and rigidity. The material contains anti oxidant .
物性信息：
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.952 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） | ISO 1133 | ||
| 190°C/2.16 kg | 0.050 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 9.0 | g/10 min | ISO 1133 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 15 | μm | |
| 割线模量 | ASTM D882 | ||
| MD : 15 μm, 吹塑薄膜 | 1250 | MPa | ASTM D882 |
| TD : 15 μm, 吹塑薄膜 | 1500 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 屈服, 15 μm, 吹塑薄膜 | 33.0 | MPa | ASTM D882 |
| TD : 屈服, 15 μm, 吹塑薄膜 | 31.0 | MPa | ASTM D882 |
| MD : 断裂, 15 μm, 吹塑薄膜 | 60.0 | MPa | ASTM D882 |
| TD : 断裂, 15 μm, 吹塑薄膜 | 56.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 15 μm, 吹塑薄膜 | 400 | % | ASTM D882 |
| TD : 断裂, 15 μm, 吹塑薄膜 | 550 | % | ASTM D882 |
| 落锤冲击(15 μm, 吹塑薄膜) | 180 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 15 μm, 吹塑薄膜 | 12 | g | ASTM D1922 |
| TD : 15 μm, 吹塑薄膜 | 60 | g | ASTM D1922 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 125 | °C | ASTM D1525 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 熔体温度 | 200 到 235 | °C |