牌号简介 About
依凡坦20-20是由乙烯和醋酸乙烯经高压自由基聚合而成的无规共聚物。高醋酸乙烯酯含量的乙烯酯20-20带来柔软、柔韧和极性。Evatane 20-20与大多数增粘树脂和蜡兼容。结合高流动性,它是一个高效和容易处理的产品热熔胶配方。Evatane 20-20也可用作原油(降凝剂)和沥青改性的添加剂。 EVATANE? 20-20 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. The high Vinyl Acetate content of EVATANE? 20-20 brings softness, flexibility and polarity. EVATANE? 20-20 is compatible with most tackifying resins and waxes. Combined with a high fluidity, it is an efficient and easy handling product for hot melt adhesives formulations. EVATANE? 20-20 can also be used as an additive for crude oil (pour point depressant) and for bitumen modification.

产品描述 Product Description
厂家:法国阿科玛 Arkema 类别:EVA EVA 用途:石油/天然气用品;沥青改性;粘合剂; 性能特点: 柔软性好; 无规共聚物; 韧性好; Good flexibility,Random copolymer,Soft
技术参数 Technical Data
物理性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
密度 Density (73°F) 0.950 g/cm3 ISO 1183
熔体质量流动速率 熔体质量流动速率
190℃,2.16kg 190℃/2.16 kg 17 to 23 g/10min ASTM D1238
190℃,2.16kg 190℃/2.16 kg 17 to 23 g/10min ISO 1133
醋酸乙烯含量 Vinyl Acetate Content 19.0 to 21.0 wt%
机械性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
邵氏硬度 邵氏硬度
邵氏 A 邵氏 A 89 ISO 868
邵氏 A 邵氏 A 89 ASTM D2240
拉伸强度 拉伸强度
断裂 断裂 17.0 MPa ISO 527-2
断裂 断裂 17.0 MPa ASTM D638
拉伸应变 拉伸应变
断裂 断裂 400 to 600 % ASTM D638
断裂 断裂 400 to 600 % ISO 527-2
热性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
维卡软化温度 Vicat Softening Temperature 46.0 ℃ ASTM D1525 2
维卡软化温度 Vicat Softening Temperature 46.0 ℃ ISO 306/A
熔融温度 Melting Temperature 83.0 ℃ ISO 11357-3
Ring and Ball Softening Point Ring and Ball Softening Point 3 3 127 ℃ ASTM E28