东莞市常平浩云塑胶经营部
Lupolen 3652 D SW 00413 HDPE
Lupolen 4261 A IM HDPE
Lupolen 4261 A Q 135 HDPE
Lupolen 4261 A Q 149 HDPE
Lupolen 4261 A Q 416 HDPE
Lupolen 4261 A SW63200 HDPE
Lupolen 4261 A HDPE
Lupolen 4261 AG Q 469 HDPE
Lupolen 4261 AG Q 470 HDPE
Lupolen 4261 AG UV 60005 HDPE
Lupolen 4261 AG UV HDPE
Lupolen 4261 AG HDPE
Lupolen 4261A IMBD HDPE
Lupolen 4261AG BD HDPE
Lupolen 4532D HDPE
Lupolen 4552D SW00413 HDPE
Lupolen 5021 D HDPE
Lupolen 5021 DX HDPE
Lupolen 5031 L Q 449 K HDPE
Lupolen 5031 L HDPE
Lupolen 5100 B HDPE
Lupolen 5231 HX HDPE
Lupolen 5261 Z HI HDPE
Lupolen 5261 Z Q 456 B HDPE
Lupolen 5261 Z Q 456 HDPE
Lupolen 5261 Z HDPE
Lupolen 5261 ZS HDPE
Lupolen 5361 A HDPE
Lupolen 5461 B Q 471 HDPE
Lupolen 5621 D HDPE
Lupolen 5621 DX HDPE
Lupolen 5661 B HDPE
Lupolen 6021 D HDPE
Lupolen 6031 M HDPE
LyondellBasell Lupolen 6021 D HDPE, Blow Molding Grade
Polymer,Thermoplastic,Polyethylene (PE),HDPE,High Density Polyethylene (HDPE), Blow Molding Grade
LyondellBasell
产品说明:
Easy flow, blow molding grade for small, rigid, thin-walled containers (up to 5 l), pots (up to 1 l), bottles and canisters (up to 5 l) for packaging mineral oil, antifreeze, brake fluid; drink bottles, handled containers (up to 6 l), etc.
Data was collected by ISO methods and originally provided by BASF. The Lupolen?? product line is now produced by Basell.
LyondellBasell Lupolen 6021 D HDPE, Blow Molding Grade 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 0.960 g/cc | 0.0347 lb/in3 | |
| 吸水率 | 0.010 % | 0.010 % | |
| 平衡吸湿 | 0.050 % | 0.050 % | |
| 熔体流动速率 | 0.265 g/10 min
@Load 2.16 kg, Temperature 190 °C
|
0.265 g/10 min
@Load 4.76 lb, Temperature 374 °F
|
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 30.0 MPa | 4350 psi | |
| 伸长率 (断裂) | = 50 % | = 50 % | |
| 屈服伸长率 | 8.0 % | 8.0 % | |
| 拉伸模量 | 1.40 GPa | 203 ksi | |
| 拉伸冲击强度 | 120 kJ/m2 | 57.1 ft-lb/in2 | |
| 拉伸蠕变模量(1 hr) | 510 MPa | 74000 psi | |
| 拉伸蠕变模量(1000 hr) | 340 MPa | 49300 psi |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 电阻率 | = 1.00e+15 ohm-cm | = 1.00e+15 ohm-cm | |
| 表面电阻 | 1.00e+14 ohm | 1.00e+14 ohm | |
| 介电常数 | 2.4
@Frequency 100 Hz
|
2.4
@Frequency 100 Hz
|
|
| 2.4
@Frequency 1e+6 Hz
|
2.4
@Frequency 1e+6 Hz
|
||
| 介电强度 | 150 kV/mm | 3810 kV/in | |
| 耗散因数 | 0.00020
@Frequency 100 Hz
|
0.00020
@Frequency 100 Hz
|
|
| 0.00020
@Frequency 1e+6 Hz
|
0.00020
@Frequency 1e+6 Hz
|
||
| 相比耐漏电起痕指数(CTI) | 600 V | 600 V |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 140 μm/m-°C
@Temperature 20.0 °C
|
77.8 μin/in-°F
@Temperature 68.0 °F
|
|
| 熔融温度 | 135 °C | 275 °F | |
| 载荷下热变形温度(0.46 MPa) | 84.0 °C | 183 °F | |
| 载荷下热变形温度(1.8 MPa) | 46.0 °C | 115 °F | |
| 维卡软化温度 | 80.0 °C | 176 °F | |
| 可燃性(UL94) | HB
@Thickness 0.400 mm
|
HB
@Thickness 0.0157 in
|
|
| 极限氧指数 | 17 % | 17 % |