拜内尔1100系列树脂是改性乙烯-醋酸乙烯聚合物。它们以颗粒形式提供,用于传统的挤出和共挤设备,设计用于加工聚乙烯(PE)树脂。拜内尔1100系列树脂可与多种材料粘合。它们最常用于粘附在PE、离聚物、EVA上,在某些情况下还可粘附在PVC、PS、HIPS和PP上。 BYNEL? Series 1100 resins are modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. BYNEL 1100 series resins adhere to a wide variety of materials. They are most often used to adhere to PE, ionomers, EVA, and in some cases PVC, PS. HIPS, and PP.

产品描述 Product Description
厂家:美国杜邦 DuPont Canada, Inc. - Dartek Division 类别:EVA EVA 加工条件:挤出 Extrusion
技术参数 Technical Data
物理性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
密度 Specific Gravity 0.950 g/cm3 ASTM D792
密度 Density 0.950 g/cm3 ISO 1183
熔体质量流动速率 熔体质量流动速率
190℃,2.16kg 190℃/2.16 kg 6.7 g/10min ASTM D1238
190℃,2.16kg 190℃/2.16 kg 6.7 g/10min ISO 1133
热性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
维卡软化温度 Vicat Softening Temperature 50.0 ℃ ASTM D1525
维卡软化温度 Vicat Softening Temperature 50.0 ℃ ISO 306
熔融峰值温度 Peak Melting Temperature 74.0 ℃ ASTM D3418
熔融温度 溶融温度
DSC DSC 74.0 ℃ ISO 3146
冰点 Freezing Point 51 ℃ ASTM D3418
备注
1 一般属性:这些不能被视为规格。