牌号简介 About
依凡坦33-25是由乙烯和醋酸乙烯经高压自由基聚合而成的无规共聚物。乙烯基醋酸盐含量高的Evatane 33-25具有柔软性、柔韧性和极性。Evatane 33-25与大多数增粘树脂和蜡兼容。它是一种高效易操作的热熔胶配方产品。Evatane 33-25与大多数填料具有高粘合强度,可用于生产HFFR化合物。它也是一种理想的基础聚合物,用于中压电缆(外部可剥离层)的半导电化合物。 EVATANE? 33-25 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. The high Vinyl Acetate content of EVATANE? 33-25 brings softness, flexibility and polarity. EVATANE? 33-25 is compatible with most tackifying resins and waxes. It is an efficient and easy handling product for hot melt adhesives formulations. EVATANE? 33-25 delivers high cohesive strength with most fillers and can be used to produce HFFR compounds. It is also an ideal base polymer for semi-conductive compounds for medium voltage cables (external strippable layer).

产品描述 Product Description
厂家:法国阿科玛 Arkema 类别:EVA EVA 用途:电线电缆应用;粘合剂; 性能特点: 柔软性好; 无规共聚物; 韧性好; Good flexibility,Random copolymer,Soft
技术参数 Technical Data
物理性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
密度 Density (73°F) 0.960 g/cm3 ISO 1183
熔体质量流动速率 熔体质量流动速率
190℃,2.16kg 190℃/2.16 kg 22 to 29 g/10min ISO 1133
190℃,2.16kg 190℃/2.16 kg 22 to 29 g/10min ASTM D1238
醋酸乙烯含量 Vinyl Acetate Content 32.0 to 34.0 wt% Internal Method
机械性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
邵氏硬度 邵氏硬度
邵氏 A 邵氏 A 67 ASTM D2240
邵氏 A 邵氏 A 67 ISO 868
拉伸强度 拉伸强度
断裂 断裂 11.0 MPa ISO 527-2
断裂 断裂 11.0 MPa ASTM D638
拉伸应变 拉伸应变
断裂 断裂 900 to 1100 % ISO 527-2
断裂 断裂 900 to 1100 % ASTM D638
热性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
维卡软化温度 Vicat Softening Temperature < 40.0 ℃ ASTM D1525 2
维卡软化温度 Vicat Softening Temperature < 40.0 ℃ ISO 306/A
熔融温度 Melting Temperature 63.0 ℃ ISO 11357-3
Ring and Ball Softening Point Ring and Ball Softening Point 3 3 119 ℃ ASTM E28
备注
1 一般属性:这些不能被视为规格。
2 压 力1 (10N)
3 NF EN 1238