Physical Properties物理性质

Metric公制数据

English英制数据

Comments测试方法

Density密度

1.36g/cc

0.0491lb/in3

ISO 1183

Water Absorption吸水率

5.2 - 5.8 %

5.2 - 5.8 %

ISO 62

Moisture Absorption at Equilibrium吸湿平衡

1.5 - 1.9 %

1.5 - 1.9 %

23°C/50% R.H.; ISO 62

Viscosity Test粘度

145cm3/g

145cm3/g

Viscosity number; ISO 307

Linear Mold Shrinkage线性收缩率

0.0055cm/cm

0.0055in/in

Melt Flow熔体流动速率

54.4g/10 min
@Load 5.00 kg,
Temperature 275 °C

54.4g/10 min
@Load 11.0 lb,
Temperature 527 °F

ISO 1133

Mechanical Properties力学性能

Metric公制数据

English英制数据

Comments测试方法

Tensile Strength, Yield屈服拉伸强度

190MPa

27600psi

ISO 527

Elongation at Yield屈服伸长率

3.0 %

3.0 %

ISO 527

Modulus of Elasticity弹性模量

10.0GPa

1450ksi

ISO 527

Flexural Strength弯曲强度

280MPa

40600psi

ISO 178

Flexural Modulus弯曲弹性模量

8.60GPa

1250ksi

ISO 178

Izod Impact, Notched悬臂梁缺口冲击强度(ISO)

11.5kJ/m2

5.47ft-lb/in2

ISO 180/A

Charpy Impact Unnotched夏比缺口试样冲击

8.50J/cm2

40.5ft-lb/in2

ISO 179/1eU

7.00J/cm2
@Temperature -30.0 °C

33.3ft-lb/in2
@Temperature -22.0 °F

ISO 179/1eU

Charpy ImPAct, Notched夏比缺口冲击

1.30J/cm2

6.19ft-lb/in2

ISO 179/1eA

1.00J/cm2
@Temperature -30.0 °C

4.76ft-lb/in2
@Temperature -22.0 °F

ISO 179/1eA

Electrical Properties电性能

Metric公制数据

English英制数据

Comments测试方法

Volume ResiSTivity体积电阻率

1.00e 13ohm-cm

1.00e 13ohm-cm

IEC 60093

Dielectric Constant介电常数

3.5
@Frequency 1.00e 6 Hz

3.5
@Frequency 1.00e 6 Hz

IEC 60250

Dissipation Factor耗散因数

0.014
@Frequency 1.00e 6 Hz

0.014
@Frequency 1.00e 6 Hz

IEC 60250

Comparative Tracking Index跟踪指数

450V

450V

Test Solution A; IEC 60112

Thermal Properties热性能

Metric公制数据

English英制数据

Comments测试方法

CTE, linear, Parallel to Flow线性热膨胀系数

0.200-0.300μm/m-°C
@Temperature 23.0 - 80.0 °C

0.111-0.167μin/in-°F
@Temperature 73.4 - 176 °F

ISO 11359

CTE, linear, Transverse to Flow线性热膨胀系数/横向

0.600-0.700μm/m-°C
@Temperature 23.0 - 80.0 °C

0.333-0.389μin/in-°F
@Temperature 73.4 - 176 °F

ISO 11359

Specific Heat Capacity比热容

1.50J/g-°C

0.359BTU/lb-°F

Thermal Conductivity导热系数

0.350W/m-K

2.43BTU-in/hr-ft2-°F

DIN 52612

Melting Point熔点

260°C

500°F

DIN 53765

Maximum Service Temperature, Air最高使用温度

240°C

464°F

Deflection Temperature at热变形温度0.46 MPa (66 psi)

250°C

482°F

ISO 75

Deflection Temperature at热变形温度1.8 MPa (264 psi)

250°C

482°F

ISO 75

Flammability, UL94阻燃等级

HB
@Thickness 1.60 mm

HB
@Thickness 0.0630 in

Processing Properties加工性能

Metric公制数据

English英制数据

Comments测试方法

Melt Temperature熔体温度

280-300°C

536-572°F

Mold Temperature模具温度

80.0-90.0°C

176-194°F